High strength bolts are widely used in the engineering field due to their good compressive properties. Accurate assessment of the ultimate capacity performance of high strength bolts under combined loading is essential to ensure the safety of steel structures in the connection zone. Existing studies are not sufficiently clear on the economic and condition-specific limits on the effects of various factors on high-strength bolts under complex stress conditions. In response to these problems, the aim of this paper is to analyse the effects of different factors on the load-bearing performance of high-strength bolts on the basis of numerical simulations. The mesoscale critical plastic strain (MCEPS) method was used on the model fracture and the accuracy of the model evaluation was verified. The effects of grade, type, diameter and bolt hole clearance on the ductile fracture behaviour of high-strength bolts were investigated. It was found that fully threaded bolts and through-hole clearances can mainly affect the load-bearing properties of high-strength bolts and increase the bolt's fracture-deformation capacity. The load-bearing performance of high-strength bolts under the influence of different factors was also compared with the Eurocode design (EC3) predictions.@en

The heat-affected zone (HAZ) is an unmelted region of a welded joint that has changed in material properties because of high temperatures during the welding process. HAZ has a lower strength than the base (parent) material (BM) and the weld metal (WM). The lower material strength is more significant if BM is made of high strength steel and the undermatching filler metal is used. Therefore, the constitutive model of HAZ is essential for predicting the mechanical behaviour of the welded joint. In this paper, a method for determining the true stress–strain relationship of HAZ is proposed. The effect of the transverse constraint on the longitudinal deformation of HAZ imposed by BM and/or WM is eliminated by a linear modification factor correlating to the true strain. Standard tensile coupon tests were used to obtain the constitutive model of HAZ using digital image correlation (DIC). The modification factor proposed for reducing the true stress is calibrated based on finite element analysis (FEA). The modified constitutive model of HAZ is validated against the experimental results obtained by DIC. The validated HAZ material property can be used in advanced numerical simulation of welded joints.@en

The coupon specimen with a transverse butt weld in the middle could be used for determining local constitutive properties of the heat-affected zone (HAZ) and the weld metal (WM) based on the digital image correlation (DIC). However, limited research is reported to demonstrate how to identify the boundary of each region in DIC results. Accordingly, it is difficult to determine the adequate gauge length for measuring the strain of each region and establishing a stress–strain curve for Finite Element Analysis (FEA) of structural problems. In this paper, a method for identifying the region's boundary is proposed based on coupon tests using three steel grades, S355, S500, and S700, corresponding to three weld matching types, match, overmatch, and undermatch, respectively. First, the hardness and the microstructure investigation were conducted to determine the region's boundary. Then, the boundary was identified based on the DIC result using the proposed method. Finally, the identified HAZ regions were verified against hardness results. Using the proposed method, the gauge length for measuring the strain of a single region, such as HAZ and WM, are determined based on the DIC results. The primary purpose is to establish the stress–strain relationship for FEA of welded joints.@en

In this paper, a numerical simulation method of mixed-mode fatigue crack propagation was explored using the extended finite element method (XFEM) and the Virtual Crack Closure Technique (VCCT). Both 2D and 3D numerical models were selected to simulate the fatigue crack propagation of steel specimens. Two coefficients were proposed to calculate the equivalent energy release rate (Geq) for a better simulation of the mixed-mode fatigue crack propagation of S355 steel. The Walker equation and the calculation formula of Geq were realized by a user-defined subroutine. A set of optimal correction coefficients of mode II energy release rate (GII) and mode III energy release rate (GIII) were quantitatively comparing the simulation results and test data. The results will contribute to fatigue crack propagation prediction of steel structures in the civil engineering field.@en

The use of high strength steel (HSS) cold-formed hollow section is of significant interest in the construction sector due to competitive costs. The accurate simulation of ductile fracture failure at the micro and macro scale is critical for improving the validity of predicting structural behaviour of HSS cold-formed hollow sections and welded joints. In this study, the ductile failure of the cold-formed S700 material is studied using the Gurson-Tvergaard-Needleman (GTN) damage model. Representative volume element (RVE) models with the void volume fraction (VVF) between 0.1% and 30% are employed to investigate the pressure dependency of the deviatoric limit stress. Different load conditions corresponding to different stress triaxiality levels are applied to unit cells with random spherical pores. The inelastic response of the unit cells are analysed, and the parameters q1, q2, and q3 in the GTN yield surface are calibrated. An equation is proposed to determine parameter q1 for different VVFs. The parameters critical VVF fc and final VVF ff are calibrated by the coupon test from the literature. Finally, the calibrated GTN model is validated against notched coupon tests. The finite element (FE) results show good agreement with the experimental results, indicating that the identified GTN model could efficiently predict the behaviour of the cold-formed HSS.@en