Iron carbides are unmistakably associated with the active phase for Fischer-Tropsch synthesis (FTS). The formation of these carbides is highly dependent on the catalyst formulation, the activation method and the operational conditions. Because of this highly dynamic behavior, studies on active phase performance often lack the direct correlation between catalyst performance and iron carbide phase. For the above reasons, an extensive in situ Mössbauer spectroscopy study on highly dispersed Fe on carbon catalysts (Fe@C) produced through pyrolysis of a Metal Organic Framework was coupled to their FTS performance testing. The preparation of Fe@C catalysts via this MOF mediated synthesis allows control over the active phase formation and therefore provides an ideal model system to study the performance of different iron carbides. Reduction of fresh Fe@C followed by low-temperature Fischer-Tropsch (LTFT) conditions resulted in the formation of the ε′-Fe_2.2C, whereas carburization of the fresh catalysts under high-temperature Fischer-Tropsch (HTFT) resulted in the formation of χ-Fe₅C₂. Furthermore, the different activation methods did not alter other important catalyst properties, as pre- and post-reaction transmission electron microscopy (TEM) characterization confirmed that the iron nanoparticle dispersion was preserved. The weight normalized activities (FTY) of χ-Fe₅C₂ and ε′-Fe_2.2C are virtually identical, whilst it is found that ε′-Fe_2.2C is a better hydrogenation catalyst than χ-Fe₅C₂. The absence of differences under subsequent HTFT experiments, where χ-Fe₅C₂ is the dominating phase, is a strong indication that the iron carbide phase is responsible for the differences in selectivity.

Heterogenization of molecular catalysts for CO₂ electroreduction has attracted significant research activity, due to the combined advantages of homogeneous and heterogeneous catalysts. In this work, we demonstrate the strong influence of the nature of the substrate on the selectivity and reactivity of electrocatalytic CO₂ reduction, as well as on the stability of the studied immobilized indium(III) protoporphyrin IX, for electrosynthesis of formic acid. Additionally, we investigate strategies to improve the CO₂ reduction by tuning the chemical functionality of the substrate surface by means of electrochemical and plasma treatment and by catalyst encapsulation in polymer membranes. We point out several underlying factors that affect the performance of electrocatalytic CO₂ reduction. The insights gained here allow one to optimize heterogenized molecular systems for enhanced CO₂ electroreduction without modification of the catalyst itself.

The oxygen evolution reaction (OER) and chlorine evolution reaction (CER) are electrochemical processes with high relevance to water splitting for (solar) energy conversion and industrial production of commodity chemicals, respectively. Carrying out the two reactions separately is challenging, since the catalytic intermediates are linked by scaling relations. Optimizing the efficiency of OER over CER in acidic media has proven especially difficult. In this regard, we have investigated the OER versus CER selectivity of manganese oxide (MnO_x), a known OER catalyst. Thin films (∼5-20 nm) of MnO_x were electrodeposited on glassy carbon-supported hydrous iridium oxide (IrO_x/GC) in aqueous chloride solutions of pH ∼0.9. Using rotating ring-disk electrode voltammetry and online electrochemical mass spectrometry, it was found that deposition of MnO_x onto IrO_x decreases the CER selectivity of the system in the presence of 30 mM Cl^- from 86% to less than 7%, making it a highly OER-selective catalyst. Detailed studies of the CER mechanism and ex-situ structure studies using SEM, TEM, and XPS suggest that the MnO_x film is in fact not a catalytically active phase, but functions as a permeable overlayer that disfavors the transport of chloride ions.

The structure and elementary composition of various commercial Fe-based MOFs used as precursors for Fischer-Tropsch synthesis (FTS) catalysts have a large influence on the high-temperature FTS activity and selectivity of the resulting Fe on carbon composites. The selected Fe-MOF topologies (MIL-68, MIL-88A, MIL-100, MIL-101, MIL-127, and Fe-BTC) differ from each other in terms of porosity, surface area, Fe and heteroatom content, crystal density and thermal stability. They are re-engineered towards FTS catalysts by means of simple pyrolysis at 500 °C under a N₂ atmosphere and afterwards characterized in terms of porosity, crystallite phase, bulk and surface Fe content, Fe nanoparticle size and oxidation state. We discovered that the Fe loading (36-46 wt%) and nanoparticle size (3.6-6.8 nm) of the obtained catalysts are directly related to the elementary composition and porosity of the initial MOFs. Furthermore, the carbonization leads to similar surface areas for the C matrix (S_BET between 570 and 670 m² g^-1), whereas the pore width distribution is completely different for the various MOFs. The high catalytic performance (FTY in the range of 1.9-4.6 × 10^-4 mol_CO g_Fe ^-1 s^-1) of the resulting materials could be correlated to the Fe particle size and corresponding surface area, and only minor deactivation was found for the N-containing catalysts. Elemental analysis of the catalysts containing deliberately added promoters and inherent impurities from the commercial MOFs revealed the subtle interplay between Fe particle size and complex catalyst composition in order to obtain high activity and stability next to a low CH₄ selectivity.

Titanium white (TiO₂) has been widely used as a pigment in the 20th century. However, its most photocatalytic form (anatase) can cause severe degradation of the oil paint in which it is contained. UV light initiates TiO₂-photocatalyzed processes in the paint film, degrading the oil binder into volatile components resulting in chalking of the paint. This will eventually lead to severe changes in the appearance of a painting. To date, limited examples of degraded works of art containing titanium white are known due to the relatively short existence of the paintings in question and the slow progress of the degradation process. However, UV light will inevitably cause degradation of paint in works of art containing photocatalytic titanium white.In this work, a method to detect early warning signs of photocatalytic degradation of unvarnished oil paint is proposed, using atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). Consequently, a four-stage degradation model was developed through in-depth study of TiO₂-containing paint films in various stages of degradation. The XPS surface analysis proved very valuable for detecting early warning signs of paint degradation, whereas the AFM results provide additional confirmation and are in good agreement with bulk gloss reduction.

The development of active, cost-effective and stable oxygen-evolving catalysts is one of the major challenges for solar-to-fuel conversion towards sustainable energy generation. Iridium oxide exhibits the best available compromise between catalytic activity and stability in acid media, but it is prohibitively expensive for large-scale applications. Therefore, preparing oxygen-evolving catalysts with lower amounts of the scarce but active and stable iridium is an attractive avenue to overcome this economical constraint. Here we report on a class of oxygen-evolving catalysts based on iridium double perovskites which contain 32 wt% less iridium than IrO₂ and yet exhibit a more than threefold higher activity in acid media. According to recently suggested benchmarking criteria, the iridium double perovskites are the most active catalysts for oxygen evolution in acid media reported until now, to the best of our knowledge, and exhibit similar stability to IrO₂.

A facile one-step method to shape covalent triazine frameworks (CTFs) for catalytic applications is reported. Phase inversion of the CTF powder by using a polyimide as a binder in a microfluidic device results in the formation of composite spheres with accessible CTF porosity and a high mechanical and thermal stability. The fabricated spheres can be used to host organometallic complexes. The obtained shaped catalysts, Ir@CTF spheres, are active and fully recyclable in the direct hydrogenation of carbon dioxide into formic acid under mild reaction conditions (20 bar and 50–90 °C) and in the dehydrogenation of formic acid.

In this combined in situ XAFS, DRIFTS, and Mössbauer study, we elucidate the changes in structural, electronic, and local environments of Fe during pyrolysis of the metal organic framework Fe-BTC toward highly active and stable Fischer-Tropsch synthesis (FTS) catalysts (Fe@C). Fe-BTC framework decomposition is characterized by decarboxylation of its trimesic acid linker, generating a carbon matrix around Fe nanoparticles. Pyrolysis of Fe-BTC at 400 °C (Fe@C-400) favors the formation of highly dispersed epsilon carbides (?′-Fe_2.2C, d_p = 2.5 nm), while at temperatures of 600 °C (Fe@C-600), mainly Hägg carbides are formed (?-Fe₅C₂, d_p = 6.0 nm). Extensive carburization and sintering occur above these temperatures, as at 900 °C the predominant phase is cementite (?-Fe₃C, d_p = 28.4 nm). Thus, the loading, average particle size, and degree of carburization of Fe@C catalysts can be tuned by varying the pyrolysis temperature. Performance testing in high-temperature FTS (HT-FTS) showed that the initial turnover frequency (TOF) of Fe@C catalysts does not change significantly for pyrolysis temperatures up to 600 °C. However, methane formation is minimized when higher pyrolysis temperatures are applied. The material pyrolyzed at 900 °C showed longer induction periods and did not reach steady state conversion under the conditions studied. None of the catalysts showed deactivation during 80 h time on stream, while maintaining high Fe time yield (FTY) in the range of 0.19-0.38 mmol_CO g_Fe ^-1 s^-1, confirming the outstanding activity and stability of this family of Fe-based FTS catalysts.