Coherent precipitation-hardened alloys often struggle to achieve both ultrahigh strength and exceptional ductility due to their limited resistance to dislocation motion and vulnerability to glide plane softening. Here, we tackle these challenges by introducing multicomponent precipitates with much increased antiphase boundary (APB) energy. In a model Ni₃Al-type (L1₂) precipitation-hardened face-centered cubic (FCC) NiCo-based alloy, we incorporate multiple elements at the Al sublattice sites within the precipitates, reducing antisite defects and enhancing ordering degree. This process yields multicomponent precipitates with an ultrahigh APB energy (~308 ± 14 millijoules per square meter), which notably strengthens the alloy. Moreover, the exceptionally high APB energy transforms the deformation mechanism from dislocation shearing to stacking fault shearing, thereby avoiding glide plane softening. These result in a tensile yield strength of 1616 ± 9 megapascals, an ultimate tensile strength of 2155 ± 22 megapascals, and a uniform elongation of 10.1 ± 0.3% for the alloy.

The combination of different phase constituents to realize a mechanical composite effect for superior strength-ductility synergy has become an important strategy in microstructure design in advanced high-strength steels. Introducing multiple phases in the microstructure essentially produces a large number of phase boundaries. Such hetero-interfaces affect the materials in various aspects such as dislocation activity and damage formation. However, it remains a question whether the characteristics of phase boundaries, such as their chemical decoration states, would also have an impact on the mechanical behavior in multiphase steels. Here we reveal a phase boundary segregation-induced strengthening effect in ultrafine-grained duplex medium-Mn steels. We found that the carbon segregation at ferrite-austenite phase boundaries can be manipulated by adjusting the cooling conditions after intercritical annealing. Such phase boundary segregation in the investigated steels resulted in a yield strength enhancement by 100–120 MPa and simultaneously promoted discontinuous yielding. The sharp carbon segregation at the phase boundaries impeded interfacial dislocation emission, thus increasing the stress required to activate such dislocation nucleation process and initiate plastic deformation. This observation suggests that the enrichment of carbon at the phase boundaries can enhance the energy barrier for dislocation emission, which provides a favorable condition for plastic flow avalanches and thus discontinuous yielding. These findings extend the current understanding of the yielding behavior in medium-Mn steels, and more importantly, shed light on utilizing and manipulating phase boundary segregation to improve the mechanical performance of multiphase metallic materials.