The relation between the microstructure and the magnetic properties of Fe2P-type (Mn,Fe)2(P,Si,B) based materials has been systematically investigated by changing the annealing temperature and time. X-ray diffraction, Scanning Electron Microscopy and Energy Dispersive X-ray Spectroscopy measurements show that the alloys contain the main Fe2P-type phase and two impurity phases of (Fe,Mn)5Si3-type and Fe2MnSi-type. Boron appears to facilitate the formation of the Fe2P-type phase during the arc-melting progress. Upon increasing the annealing temperatures from 1123 to 1423 K, the Curie temperature (TC) decreases from 302.0 to 270.5 K in the Mn1.15Fe0.85P0.55Si0.45 alloys and the magnetic-entropy change (ΔSM) increases linearly with annealing temperature. For the Mn1.15Fe0.85P0.52Si0.45B0.03 alloys annealed at 1423 K for different times, TC decreases from 263.8 and 232.8 K with increasing annealing time and ΔSM reaches a maximum value after annealing for 48 h. The differences in the annealing temperature and time influence the Si content in the Fe2P-type phase of the alloys and determine TC, the thermal hysteresis and the magneto-elastic transition.@en

A rotary active magnetic regeneration refrigerator prototype named FAME Cooler was developed for studying the performance of different magnetocaloric materials in a realistic practical environment. The rotary magnetic field source generates an average magnetic field of 0.875 T within a volume of 0.71 l The regenerator is designed asymmetrically and holds in total 1.18 kg of gadolinium spheres for a first performance test. Combined with a real-time controlled programmable solenoid-valves system, different working parameters or thermodynamic cycles can be applied. In the performance test, while the temperature of system hot side was fixed at 295 K, under a utilization condition of 0.25, this prototype achieved a maximum zero-span cooling power of 162.4 W, and a zero-power temperature span of 11.6 K. Under a utilization condition of 0.15, a maximum COP of 1.85 was reached. These performance metrics are comparable with existing magnetic heat pump devices of the same scale.@en