The corrosion inhibiting effect of lithium carbonate has been studied over the pH range relevant for atmospheric corrosion conditions at the polymer/metal interface. It is demonstrated that lithium carbonate offers optimum corrosion protection under moderately alkaline conditions attributed to the formation of a protective layer identified as aluminum-lithium layered double hydroxide. It is proposed that an active-to-passive transition occurs in the presence of lithium carbonate under moderately alkaline conditions where anodic dissolution of the aluminum matrix is an important step prior to the formation of the protective layer. After prolonged exposure, the protective layer is uniformly formed on the surface of AA2024-T3 and lithium containing AA2198-T8 covering both the matrix and active intermetallic particles thus hindering further corrosion reactions.@en

This work presents the synthesis of nanostructured hollow polyaniline (PANI) capsules and their application for encapsulation of corrosion inhibitor 2-Mercaptobenzothiazole (MBT). The pH-triggered release of MBT from the capsules was evidenced using UV–vis and Surface Enhanced Raman Spectroscopy (SERS). Incorporation of MBT loaded PANI capsules into epoxy ester coating on AA2024-T3 resulted in a protective system with self-healing ability confirmed by Electrochemical Impedance Spectroscopy (EIS) and Scanning Vibrating Electrode Technique (SVET). The results showed that the incorporation of MBT-loaded PANI capsules into the coating has significantly improved its corrosion protection performance due to the interesting smart characteristics of PANI capsules.@en