This study investigated the deterioration of a lubricant-infused anodic aluminium oxide surface in a 1 M NaCl solution for ∼200 days. Direct observation by cryo-SEM and quantitative analyses by UV spectroscopy and EIS revealed that the long-term deterioration of the lubricant-infused surface was divided into two stages: the surface-adhered lubricant layer gradually dissolved at a constant rate until the substrate was exposed; afterwards the lubricant infused in the nanochannels began to diffuse and was depleted after ∼200 days. The EIS results also revealed that the defects reduced the corrosion resistance of the lubricant-infused surface considerably.

Recently, lubricant-infused surfaces (LIS) have emerged as a prominent class of surface technology for antifouling, anti-icing and anticorrosion applications. However, long-term corrosion exposure and mechanical damages may deteriorate the practical performance of LIS during application. In this study, a robust LIS was fabricated by the vacuum impregnation of mineral oil into anodized aluminum oxide (AAO) nanochannels with a depth of 50 μm. The impregnation of the lubricant through the entire depth of the high-aspect-ratio nanochannels was visualized under cryo-scanning electron microscopy (cryo-SEM) and also confirmed by weight gain measurements. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP) tests showed that the lubricant stored in the deep nanochannels of LIS can provide excellent corrosion protection during long-term immersion. Furthermore, the as-prepared LIS demonstrated superior resistance to mechanical damage due to a self-healing effect by the lubricant. As shown by cryo-SEM observation and PDP tests, the micro-cracks formed on the LIS can be instantaneously repaired by the in-flow of the oil from the surrounding surface. In the tribological tests, the LIS also presented high wear resistance and superior mechanical durability.