Corrosion Mechanism of Microporous Nickel-Chromium Coatings
Part II. SECM Study Monitoring Cu<sup>2+</sup>and Oxygen Reduction
The corrosion mechanism of microporous nickel-chromium multilayer coatings was studied at localised scale by Scanning Electrochemical Microscopy (SECM) after exposure to an aggressive electrolyte (chloride-based one at pH 3.1 containing cupric ions). The open circuit potential wa
...
The impact of the pH on the corrosion of microporous nickel-chromium coatings has been explored at localised scale by Scanning Electrochemical Microscopy and validated by potentiodynamic polarisation measurements. Results not only reveal the correlation between both techniques bu
...