This work presents a study of p-type passivating contacts based on SiCx formed via a rapid thermal processing (RTP) step, using conditions compatible with the firing used to sinter screen-printed metallization pastes in industry. The contributions of the two interfaces (wafer/contact and contact/metal) to the contact resistivity are first decorrelated, identifying tunnelling at the wafer interface as the main contribution. We then investigate the influence of the active dopant concentration on the contact resistivity and the SiCx sheet resistance and propose strategies to reduce both resistances by increasing the thermal budget applied during RTP. Lastly, we discuss potentials and limitations of implementing the investigated stacks as rear side contacts of p-type devices with localized metallization. We demonstrate that increasing the thermal budget during RTP can effectively mitigate resistive losses and enhance contact performance and we show that an oxide layer that can withstand high thermal budgets is the key factor for obtaining simultaneously high passivation quality and good electrical properties. We investigate three different oxide types grown by HNO3 immersion, UV-O3 exposure and N2O plasma oxidation. The latter is demonstrated to be a promising candidate for an application in devices fabricated with high RTP thermal budget.@en

The integration of passivating contacts based on a highly doped polycrystalline silicon (poly-Si) layer on top of a thin silicon oxide (SiOx) layer has been identified as the next step to further increase the conversion efficiency of current mainstream crystalline silicon (c-Si) solar cells. However, the interrelation between the final properties of poly-Si/SiOx contacts and their fabrication process has not yet been fully unraveled, which is mostly due to the challenge of characterizing thin-film stacks with features in the nanometric range. Here, we apply in situ X-ray reflectometry and diffraction to investigate the multiscale (1 Å-100 nm) structural evolution of poly-Si contacts during annealing up to 900 °C. This allows us to quantify the densification and thinning of the poly-Si layer during annealing as well as to monitor the disruption of the thin SiOx layer at high temperature >800 °C. Moreover, results obtained on a broader range of thermal profiles, including firing with dwell times of a few seconds, emphasize the impact of high thermal budgets on poly-Si contacts' final properties and thus the importance of ensuring a good control of such high-temperature processes when fabricating c-Si solar cells integrating such passivating contacts. Overall, this study demonstrates the robustness of combining different X-ray elastic scattering techniques (here XRR and GIXRD), which present the unique advantage of being rapid, nondestructive, and applicable on a large sample area, to unravel the multiscale structural evolution of poly-Si contacts in situ during high-temperature processes.@en