To purify severe air pollution in traffic-intensive urban areas and tunnels, an innovative type of photocatalytic micro-surfacing mixture (PMM) was designed, which was enhanced by polypropylene (PP) fiber and nano-TiO2. In this work, the road performance of sixteen PMMs with the different contents of PP and nano-TiO2 were evaluated by wet-track abrasion test, wheel rutting deformation test and low-temperature splitting test. The vehicle exhaust (VE) gas degradation capacity of sixteen PMMs was characterized under ultraviolet (UV) light and visible light conditions. The life cycle assessment (LCA) methodology was applied to evaluate the environmental impact of PMM. The results showed that the road performances of PMM were improved with the increase of the PP fibers amount. The VE gas degradation capacity was significantly enhanced with the increase of nano-TiO2 amount. PMM with 0.2 wt% PP fibers and 60 wt% replacement of mineral filler with nano-TiO2 was a viable alternative to improve photocatalytic degradation of VE in pavement engineering. In addition, the modified micro-surfacing mixture facilitates a significant reduction in energy consumption and greenhouse gas emissions.@en

The proper disposal of steel slag has always been a great challenge for the metallurgical industry in China and around the world. In this work, the steel slag aggregate (SSA) was surface pretreated (PSSA) and applied into asphalt mixture. The adhesive behavior between the bitumen and five different types of aggregates (i.e., limestone, diorite, diabase, SSA, PSSA) were evaluated based on the contact angle and binder bond strength tests. The pavement performance of three asphalt mixtures which contain normal aggregate, SSA and PSSA respectively, was analyzed by Marshall stability test, wheel-tracking rutting test, low-temperature bending creep test and water sensitivity test. The results showed that surface modification can improve the surface properties of SSA, reduce its contact angle with bitumen, and eventually lead to the improvement of adhesion between them. In addition to the satisfied low-temperature properties, PSSA was found to significantly improve the anti-rutting property and reduce the water sensitivity of asphalt mixture. This work is expected to promote an alternative application for recycling of SSA in pavement engineering.@en