The continuous increasing demand of public transportation capacity requires the railway network operating in tight schedule. The high transporting volumes not only aggravate the degradation of railway infrastructure but also shorten the time fo r maintenance. Well-arranged infrastructure maintenance contributes to the budget reduction and reliability improvement. With the purpose of key parameters investigation in the turnout crossing degradation process, a series of subsequent measurements using instrumented crossing system (ESAH-M) on a 1:15 railway turnout at various stages were performed. The results indicate that wheel/rail impact area narrowed with deepened rail wear. This narrowing is a signal of rail damage. Frequency band pass filtered results describe the condition development of different structures in the turnout crossing section in the test period. Series of mo re systematic crossing measurements are in progress in a test section in the Netherlands. The ultimate purpose of this study is to form the crossing degradation function to be implemented in the structural health monitoring system (SHMS) for railway turnouts developed at the TU Delft.@en

In this paper a numerical procedure for analysis of rolling contact fatigue crack initiation and fatigue life prediction for the railway turnout crossing is presented. To analyse wheel–rail interaction, a three-dimensional explicit finite element (FE) model of a wheelset passing a turnout crossing is developed to obtain the dynamic responses such as the contact forces, displacements and accelerations as well as the stresses and strain in the crossing nose. The material model accounting for elastic–plastic isotropic and kinematic hardening effects in rails is adopted. The fatigue life of the rails is defined as the time to rolling contact fatigue crack initiation. In predicting the fatigue life Jiang and Sehitoglu model is used, which is based on the critical plane approach. Using the FE simulation results the ten critical locations on the crossing nose susceptible to crack initiation are determined first. Then, using the fatigue model the critical planes in these locations are obtained and the number of cycles to fatigue crack initiation is calculated for each location, based on which the most decisive location and the crossing life is determined. The results of the numerical simulations are presented and discussed.@en

In this paper, the effects of repair welding and grinding, which are currently the main components used in the maintenance of crossings, on the performance of crossings are analyzed. It has been observed that sometimes the welding and grinding activities that directly affect the geometry of the crossings and/or material properties can have negative effects on the performance and ultimately on the service life of the crossings. In this paper, the effect of the changes of geometry has been studied experimentally, while the effect of the changes in the material properties has been analyzed using a numerical model. When grinding the shape of the crossing nose, the resulting profile can deviate from the original one. To analyze the geometry-related effects of welding and grinding, the geometry of crossings (cross-sectional profiles) as well as the corresponding dynamic accelerations due to passing trains are measured before and after the welding and grinding activities. Based on the comparison of the measured accelerations, the performance of the measured crossings has been assessed. Also, a welding repair that is not properly performed can lead to undesirable changes in the material properties of the rails, resulting in defects in rails. The material-related effects of the welding and grinding are studied using the three-dimensional explicit finite element model wherein a wheelset moves over a railway crossing. To understand the microstructure of the welding defect and provide an input for the numerical model, the results of ultrasonic and microscopic analyses of some welded crossings are presented first. Then, a number of the numerical simulations of the crossing with the welding defect are performed to investigate the failure mechanism of the crossing. Furthermore, assessment using the fatigue model (coupled with the finite element model) that accounts for the ratcheting behavior of material by calculating a number of the load cycles to the crack initiation is performed. Finally, conclusions on the effects of changes in geometry and material of the crossings due to repair welding and grinding are given. @en