This study characterized the morphology, high-temperature property, rheological property, adhesion, cohesion, and chemical component of asphalt binder under aqueous solutions of different pH values. Then the physicochemical properties of asphalt binder were comprehensively evaluated by the improved radar chart. The properties of asphalt binder stripped layer-by-layer were explored to elucidate its gradient damage behaviors. The results indicate that the pH 3 solution reveals the greatest impact on the morphology of 90 asphalt (90 A) and styrene-butadiene-styrene modified asphalt (SBS MA), leading to the wide cracks on 90 A and the network cracks on SBS MA. The comprehensive assessment index of 90 A exposed to pH 3, pH 5, pH 7, pH 9, and pH 11 solutions can be reduced by 20.8%, 20.2%, 1.5%, 14.0%, and 25.5%, respectively. While for SBS MA, its corresponding values variation are 23.2%, 17.7%, 4.6%, 8.7%, and 13.0%, respectively. The acid solutions significantly affect the comprehensive properties of 90 A, but their pH value has little effect. 90 A exposure to the higher pH value of alkali solution reveals the worse comprehensive properties. Acid solute and alkali solute can aggravate the effect of aqueous solution on the comprehensive properties of SBS MA, and the degree of aggravation increases with the increase of solute concentration. The properties of asphalt binders exhibit varied gradient damage behaviors under different solute environments. The most serious damage occurs at 25–50 µm of 90 A and 0–50 µm of SBS MA. This study facilitates an accurate understanding of the mechanism of pavement distresses and composition design and construction utilization of asphalt binders.

@en

Moisture erosion is one of the key factors leading to asphalt pavement damage, and the erosion depth indicates the moisture damage level but it is usually neglected. In order to study the moisture erosion and the erosion depth, this study characterized the chemical structure, rheological property and adhesion property of asphalt at different depths after immersion for different periods. To further explore the diffusion mechanism of eroded asphalt, a Log-log numerical model was established based on the Fick's second law to calculate the diffusion coefficient throughout the depth. The results indicate that it takes just four hours for water to penetrate a 25 μm asphalt film. The relation between erosion depth and immersion period presents three stages, and the process can be fitted with a polynomial model. At the macroscopic level, there is a lag between the changes in adhesion property with chemical structure and rheological property. Additionally, the periodicity of moisture erosion process was verified by the calculation of diffusion factor. In summary, the diffusion mechanism of eroded asphalt by moisture can provide a theoretical basis for the development of laboratory moisture erosion test specification, thus avoiding the waste of raw materials.

@en

Traditional asphalt mixtures can't absorb microwave energy efficiently, which limits the development of microwave heating technology in the field of road maintenance. Based on the microwave heating characteristics of basalt aggregates, the overall microwave self-healing rate of the asphalt mixture can be enhanced. The basalt was tested by XRF, XPS, XRD and electromagnetic parameters to reveal its microwave heating mechanism. Through the heating rate test, SCB test and fatigue test of asphalt mixture, its heating characteristics, flexural strength, fatigue resistance and self-healing performance were studied. The results showed that the excellent wave-absorbing properties of basalt are highly correlated with the elements of Si, Fe and Al. Its TanδM was slightly larger than TanδE, which indicated that basalt can absorb microwave energy through dielectric loss and magnetic loss. The aggregate type and particle size both affected the microwave heating rate of the aggregates. After microwave heating, the flexural strength and fatigue resistance of asphalt mixture with basalt and limestone aggregates can recover at least 65% and 23% respectively.@en

A self-compacting steel slag epoxy resin concrete (SERC) was designed with steel slag as aggregate and epoxy resin as binder for rapid repair of road expansion joints and pavement. At the same time, a group of self-compacting basalt epoxy resin concrete (BERC) with basalt as coarse aggregate and limestone as fine aggregate was set up as the control group. The element analysis and micro morphology of SERC and BERC were studied by X-ray fluorescence spectrometry (XRF) and scanning electron microscope (SEM) to reveal the strength-forming mechanism of the two epoxy resin concretes. The cube compression test and Marshall stability test were used to study the effect of the strength formation rate and temperature of SERC and BERC on the strength. In addition, the high-temperature stability, low-temperature crack resistance, water damage resistance, fatigue resistance and interlayer bonding properties of SERC and BERC were also studied. The results showed that both SERC and BERC have good mechanical properties, high temperature properties and good bonding properties, and the low-temperature crack resistance and fatigue properties of SERC are better than that of BERC. According to the verification of the actual project that has been in service for one year, SERC can be perfectly used for road expansion joints.

@en

To meet the needs of the road industry for maintenance operations, a new cement emulsified bitumen mixture (CEBM) with early-strength, self-compacting, and room-temperature construction characteristics was designed. The strength formation mechanism of CEBM was revealed with a scanning electron microscope (SEM) and the surface free energy (SFE) theory. The mechanical properties and road performance of the CEBM were investigated extensively. The results show that before the demulsification of emulsified bitumen, the SFE of the bitumen–aggregate–water three-phase system was reduced due to the replacement of the bitumen–aggregate interface with water. The adhesion work between the emulsified bitumen and the aggregate is negative, which means the adhesion between the emulsified bitumen and the aggregate will not occur spontaneously due to the existence of water. The liquid emulsified bitumen improves the workability of the mixture and ensures that the mixture can be evenly mixed and self-compacted. After demulsification, the work of adhesion between the residual bitumen and the aggregate is positive, which means residual bitumen and aggregate can bond spontaneously. In addition, the hydration products of cement and aggregate form a skeleton, and the emulsified bitumen film wraps and bonds the cement and aggregate together, creating strength. The emulsified bitumen, cement content, and curing conditions have significant effects on the stability of CEBM. The recommended dosage of emulsified bitumen and cement is 8% and 8–10%, respectively. This material integrates the hardening effect of cement and the viscoelastic performance of bitumen and has good workability, mechanical properties, and road performance. Therefore, the CEBM is technically feasible for application to bitumen pavement.

@en