Sufficient liquid feeding under constrained solidification conditions like, those experienced in welding and casting, is vital to avoid solidification cracking. We present the results of unique in-situ experimental observations of liquid feeding in a solidifying steel melt pool. Liquid feeding was observed in the inter-cellular regions during the terminal stage of solidification. An average liquid flow speed of 450–500 μm s⁻¹ was found. A pressure difference of the order of 10⁴ Pa is calculated to cause the liquid flow. The rate of solidification shrinkage and the rate of deformation were found to be less than the rate of liquid feeding.

In situ high-temperature laser scanning confocal microscopy is applied to study solidification cracking in a TRIP steel. Solidification cracking was observed in the interdendritic region during the last stage of solidification. Atom probe tomography revealed notable enrichment of phosphorus in the last remaining liquid. Phase field simulations also confirm phosphorus enrichment leading to severe undercooling of more than 160 K in the interdendritic region. In the presence of tensile stress, an opening at the interdendritic region is difficult to fill with the remaining liquid due to low permeability and high viscosity, resulting in solidification cracking.