As the voltage levels of solid-state transformers (SSTs) increase using medium-voltage switches, high-frequency transformers (HFTs) used inside SSTs are subjected to increased electrical stress. This stress, characterized by high voltage, high-frequency pulsewidth modulation (PWM) voltage, can cause insulation partial discharge (PD) and potentially lead to failure of the HFT insulation system. While PD behavior under power-frequency sinusoidal voltage has been extensively studied, the behavior of HFT insulation under PWM square pulse conditions is less well understood. To address this gap, a high voltage high-frequency PWM voltage PD test platform is developed and high-frequency current transformer (HFCT) and ultra-high-frequency (UHF) antenna are used for PD signal detection. PD tests are performed under a variety of PWM conditions including PWM frequency, rise time, voltage amplitude, and different insulation layers to thoroughly investigate the HFT insulation behavior. The PD characteristics of repetitive PD inception voltage and phase-resolved PD patterns at different PWM conditions are recorded and analyzed under PWM conditions. In addition, this article explores the underlying PD mechanisms of the HFT insulation under high-frequency PWM stress, providing insights to explain the observed test results. The findings from this research provide essential references and lay a solid foundation for future advances in optimal design, health monitoring, reliability analysis, and lifetime prediction for HFTs in power electronics applications.

Copper and zinc were recovered from waste diamond cutters through leaching with an ammonia–ammonium sulfate system and air as an oxidant. The effects of experimental parameters on the leaching process were investigated, and the potential–pH (E–pH) diagrams of Cu–NH₃–SO₄ ²⁻–H₂O and Zn–NH₃–SO₄ ²⁻–H₂O at 25°C were drawn. Results showed that the optimal parameters for the leaching reaction are as follows: reaction temperature, 45°C; leaching duration, 3 h; liquid-to-solid ratio, 50:1 (mL/g); stirring speed, 200 r/min; ammonia concentration, 4.0 mol/L; ammonium sulfate concentration, 1.0 mol/L; and air flow rate, 0.2 L/min. The results of the kinetics study indicated that the leaching is controlled by the surface chemical reaction at temperatures below 35°C, and the leaching is controlled by diffusion through the product layer at temperatures above 35°C.