Two-photon polymerization (2PP) is an additive manufacturing technology capable of producing polymeric 3D nano- to mesoscale structures with design flexibility and sub-micron resolution. This study investigates the influence of 2PP printing parameters on the morphology and mechanical properties of solid and porous microstructures fabricated from three commercial resins: IP-Q, IP-S, and IP-polydimethylsiloxane (IP-PDMS). To evaluate micromechanical behavior, micropillar compression tests are conducted using IP-Q, which has not been extensively characterized. Porous structures retained 80–85% of the stiffness of solids for IP-Q and IP-S, and 50% for IP-PDMS. Fourier transform infrared spectroscopy showed degrees of conversion of 38% for IP-Q and 61% for IP-S and IP-PDMS. The optimal printing parameters for IP-Q micropillars were a laser power of 50 mW, slicing distance (s) of 1.2 μm, and hatching distance (h) of 1 μm. These settings correspond to a peak laser intensity of 1.58 × 10⁻¹¹ W cm⁻², a focal spot diameter (dxy) of 3.17 μm, a Rayleigh length (zR) of 10.13 μm, and a voxel overlap (δ) of 0.6. These conditions yielded a Young's modulus of 3.7 GPa and yield strength of 75.21 MPa. Overall, the findings emphasize the challenges of parameter optimization when introducing porosity and comparing materials. The results provide a systematic framework for tailoring 2PP processing to guide biomedical microdevice design.

Ocean acidification is a threat to the net growth of tropical and deep-sea coral reefs, due to gradual changes in the balance between reef growth and loss processes. Here we go beyond identification of coral dissolution induced by ocean acidification and identify a mechanism that will lead to a loss of habitat in cold-water coral reef habitats on an ecosystem-scale. To quantify this, we present in situ and year-long laboratory evidence detailing the type of habitat shift that can be expected (in situ evidence), the mechanisms underlying this (in situ and laboratory evidence), and the timescale within which the process begins (laboratory evidence). Through application of engineering principals, we detail how increased porosity in structurally critical sections of coral framework will lead to crumbling of load-bearing material, and a potential collapse and loss of complexity of the larger habitat. Importantly, in situ evidence highlights that cold-water corals can survive beneath the aragonite saturation horizon, but in a fundamentally different way to what is currently considered a biogenic cold-water coral reef, with a loss of the majority of reef habitat. The shift from a habitat with high 3-dimensional complexity provided by both live and dead coral framework, to a habitat restricted primarily to live coral colonies with lower 3-dimensional complexity represents the main threat to cold-water coral reefs of the future and the biodiversity they support. Ocean acidification can cause ecosystem-scale habitat loss for the majority of cold-water coral reefs.