Magnesium nanoparticles coated by a native oxide shell and decorated by palladium clusters were synthesized by the inert gas condensation technique. The kinetics and thermodynamics of hydrogen sorption were investigated by Sieverts measurements at high temperature and by optical hydrogenography close to ambient temperature. The structure and morphology of the nanoparticles were studied by electron microscopy and X-ray diffraction both in the as-prepared state and after hydrogen sorption cycles.@en

Magnesium thin films covered with a layer of Pd absorb hydrogen at much higher pressures than bulk Mg. Such an effect was originally explained as a consequence of elastic clamping on Mg by the capping Pd layer. An alternative interpretation later suggested that the pressure increase could originate from simple alloying between Mg and Pd. Here we resolve this controversy by measuring the hydrogenation and dehydrogenation isotherms of Mg-Pd thin film alloys over a wide range of compositions. Our results disentangle the effects of elastic clamping and alloying and highlight the role of plastic deformations.@en

We tune the thermodynamics of hydrogen absorption in Mg by means of elastic clamping. The loading isotherms measured by hydrogenography show that Mg films covered with Mg-alloy-forming elements, such as Pd and Ni, have hydrogen plateau pressures more than 2 orders of magnitude higher than bulk Mg at the same temperature. An elastic model allows us to interpret the Mg thickness dependence of the hydrogen plateau pressure. Our results suggest an alternative route for the development of new hydrogen storage materials with optimized thermodynamic properties.@en