The microstructure, shear behaviour and hardness of the SnBi/SACBN/Cu solder joint before and after isothermal ageing were investigated in comparison with the SnBi/Cu and SACBN/Cu solder joints. The experimental results indicated that the pre-soldered SACBN joint had a significant effect on the formation and growth of the β-Sn grains in the SnBi bulk solder. The brittleness of the SnBi/SACBN/Cu composite solder joint was also suppressed and its failure mode transformed from brittle failure to brittle-ductile failure after reflow. However, the shear strength and failure mode of the SnBi/SACBN/Cu composite solder joint became similar to those of the SnBi/Cu joints after 600 h isothermal ageing. The shear strength of the three kinds of solder joints decreased after isothermal ageing, but the SnBi/SACBN/Cu composite solder joint showed higher shear strength than SnBi/Cu did during ageing. The shear strength of the composite solder joint was 67.1MPa after ageing. Due to the diffusion of elements in the isothermal ageing process, the microstructure of the composite solder joint was significantly coarsened after ageing for 600 hours. This phenomenon further led to the decrease of the hardness and shear strength of the three kinds of solder joints.@en

Sn-Ag-x solders were used as the interfacial layers between SnBi solder and Cu substrate. The effects of Sn-Ag-x layers on the solderability, microstructure, and mechanical properties of SnBi solder joint were investigated. Experimental results indicate that all the barrier layers have positive effects on improving the wettability of SnBi solder. The relative area and grain size of β-Sn was enlarged due to the addition of Sn-Ag-x layers. Meanwhile, the addition of the interfacial layers decreased the hardness of the SnBi solder joint. The addition of Sn-Ag-x layers increased the thickness of the interfacial intermetallic compound (IMC) but had limited effects on the shear force of the SnBi solder joint. Due to the addition of the interfacial layers, the brittleness of the SnBi/Cu solder joints during the shear test was slightly suppressed.@en