The authors regret an error in the abstract of the published article: the text ‘‘(i) the Schottky emission mechanism at a low reverse voltage (0–1 V) before the current is fully turned on.’’ should be changed to ‘‘(i) the Schottky emission mechanism at a low reverse voltage (0 to 1 V) before the current is fully turned on.’’ This change does not affect the main conclusions of the manuscript. The authors would like to apologize for any inconvenience caused. The Royal Society of Chemistry apologises for these errors and any consequent inconvenience to authors and readers.

Recent research focusing on wide-bandgap and two-dimensional materials with a Schottky junction has provided a new concept for ultraviolet photodetectors. However, the working mechanism of the Schottky junction-based detector varies depending on the photosensitive materials used and the device structure. We demonstrated a TiO₂/AlGaN/GaN heterostructure-based photodetector with a Schottky junction, integrating an ultraviolet photosensitive TiO₂ nanolayer, a two-dimensional electron gas (2DEG) field effect transistor, and a metal-semiconductor Schottky diode. The spectral response wavelength region of the detector is 200-365 nm and the peak responsivity is 37.396 A W⁻¹ at −5 V bias under 240 nm UV illumination, respectively. Meanwhile, a peak photo-to-dark current ratio (PDCR) of 5.1 × 10² at −2 V bias voltage was observed under 274 nm UV irradiation. This Schottky-based 2DEG heterostructure detector can realize three dominant working principles: (i) the Schottky emission mechanism at a low reverse voltage (0-1 V) before the current is fully turned on, (ii) the Poole-Frenkel emission mechanism at a medium reverse voltage (−1 to −2 V) with peak PDCR, and (iii) the Fowler-Nordheim tunneling mechanism at a high reverse voltage (>−2 V) with a high responsivity. Continuous cycle response measurement results indicate that the detectors have good response repeatability and reliability. The characteristics of response wavelength, responsivity, and stability show that the detector can be used for several commercial applications, including sunscreen UV monitoring and LED sterilization light source detection.