Journal article
(2021)
-
Guangdao Zhang, Pengyu Zhao, Lin Lin, Limei Qin, Zhiguang Huan, M.A. Leeflang, A.A. Zadpoor, J. Zhou, Lin Wu
Background
Given their highly adjustable and predictable properties, three-dimensional(3D) printed geometrically ordered porous biomaterials offer unique opportunities as orthopedic implants. The performance of such biomaterials is, however, as much a result of the surface properties of the struts as it is of the 3D porous structure. In our previous study, we have investigated the in vitro performances of selective laser melted (SLM) Ti-6Al-4V scaffolds which are surface modified by the bioactive glass (BG) and mesoporous bioactive glass (MBG), respectively. The results demonstrated that such modification enhanced the attachment, proliferation, and differentiation of human bone marrow stromal cells (hBMSC). Here, we take the next step by assessing the therapeutic potential of 3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications for bone regeneration in a rabbit bone defect model.
Methods
3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications were implanted into the femoral condyle of the rabbits, the Ti-6Al-4V scaffolds without surface modification were used as the control. At week 3, 6, and 9 after the implantation, micro-computed tomography (micro-CT) imaging, fluorescence double-labeling to determine the mineral apposition rate (MAR), and histological analysis of non-decalcified sections were performed.
Results
We found significantly higher volumes of regenerated bone, significantly higher values of the relevant bone morphometric parameters, clear signs of bone matrix apposition and maturation, and the evidence of progressed angiogenesis and blood vessel formation in the groups where the bioactive glass was added as a coating, particularly the MGB group.
Conclusions
The MBG coating resulted in enhanced osteoconduction and vascularization in bone defect healing, which was attributed to the release of silicon and calcium ions and the presence of a nano-mesoporous structure on the surface of the MBG specimens. ...
Given their highly adjustable and predictable properties, three-dimensional(3D) printed geometrically ordered porous biomaterials offer unique opportunities as orthopedic implants. The performance of such biomaterials is, however, as much a result of the surface properties of the struts as it is of the 3D porous structure. In our previous study, we have investigated the in vitro performances of selective laser melted (SLM) Ti-6Al-4V scaffolds which are surface modified by the bioactive glass (BG) and mesoporous bioactive glass (MBG), respectively. The results demonstrated that such modification enhanced the attachment, proliferation, and differentiation of human bone marrow stromal cells (hBMSC). Here, we take the next step by assessing the therapeutic potential of 3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications for bone regeneration in a rabbit bone defect model.
Methods
3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications were implanted into the femoral condyle of the rabbits, the Ti-6Al-4V scaffolds without surface modification were used as the control. At week 3, 6, and 9 after the implantation, micro-computed tomography (micro-CT) imaging, fluorescence double-labeling to determine the mineral apposition rate (MAR), and histological analysis of non-decalcified sections were performed.
Results
We found significantly higher volumes of regenerated bone, significantly higher values of the relevant bone morphometric parameters, clear signs of bone matrix apposition and maturation, and the evidence of progressed angiogenesis and blood vessel formation in the groups where the bioactive glass was added as a coating, particularly the MGB group.
Conclusions
The MBG coating resulted in enhanced osteoconduction and vascularization in bone defect healing, which was attributed to the release of silicon and calcium ions and the presence of a nano-mesoporous structure on the surface of the MBG specimens. ...
Background
Given their highly adjustable and predictable properties, three-dimensional(3D) printed geometrically ordered porous biomaterials offer unique opportunities as orthopedic implants. The performance of such biomaterials is, however, as much a result of the surface properties of the struts as it is of the 3D porous structure. In our previous study, we have investigated the in vitro performances of selective laser melted (SLM) Ti-6Al-4V scaffolds which are surface modified by the bioactive glass (BG) and mesoporous bioactive glass (MBG), respectively. The results demonstrated that such modification enhanced the attachment, proliferation, and differentiation of human bone marrow stromal cells (hBMSC). Here, we take the next step by assessing the therapeutic potential of 3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications for bone regeneration in a rabbit bone defect model.
Methods
3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications were implanted into the femoral condyle of the rabbits, the Ti-6Al-4V scaffolds without surface modification were used as the control. At week 3, 6, and 9 after the implantation, micro-computed tomography (micro-CT) imaging, fluorescence double-labeling to determine the mineral apposition rate (MAR), and histological analysis of non-decalcified sections were performed.
Results
We found significantly higher volumes of regenerated bone, significantly higher values of the relevant bone morphometric parameters, clear signs of bone matrix apposition and maturation, and the evidence of progressed angiogenesis and blood vessel formation in the groups where the bioactive glass was added as a coating, particularly the MGB group.
Conclusions
The MBG coating resulted in enhanced osteoconduction and vascularization in bone defect healing, which was attributed to the release of silicon and calcium ions and the presence of a nano-mesoporous structure on the surface of the MBG specimens.
Given their highly adjustable and predictable properties, three-dimensional(3D) printed geometrically ordered porous biomaterials offer unique opportunities as orthopedic implants. The performance of such biomaterials is, however, as much a result of the surface properties of the struts as it is of the 3D porous structure. In our previous study, we have investigated the in vitro performances of selective laser melted (SLM) Ti-6Al-4V scaffolds which are surface modified by the bioactive glass (BG) and mesoporous bioactive glass (MBG), respectively. The results demonstrated that such modification enhanced the attachment, proliferation, and differentiation of human bone marrow stromal cells (hBMSC). Here, we take the next step by assessing the therapeutic potential of 3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications for bone regeneration in a rabbit bone defect model.
Methods
3D printed Ti-6Al-4V scaffolds with BG and MBG surface modifications were implanted into the femoral condyle of the rabbits, the Ti-6Al-4V scaffolds without surface modification were used as the control. At week 3, 6, and 9 after the implantation, micro-computed tomography (micro-CT) imaging, fluorescence double-labeling to determine the mineral apposition rate (MAR), and histological analysis of non-decalcified sections were performed.
Results
We found significantly higher volumes of regenerated bone, significantly higher values of the relevant bone morphometric parameters, clear signs of bone matrix apposition and maturation, and the evidence of progressed angiogenesis and blood vessel formation in the groups where the bioactive glass was added as a coating, particularly the MGB group.
Conclusions
The MBG coating resulted in enhanced osteoconduction and vascularization in bone defect healing, which was attributed to the release of silicon and calcium ions and the presence of a nano-mesoporous structure on the surface of the MBG specimens.
Journal article
(2020)
-
Pengyu Zhao, Yaqin Liu, Tian Li, Yanling Zhou, Sander Leeflang, Lei Chen, Chengtie Wu, Jie Zhou, Zhiguang Huan
Titanium alloy scaffolds have recently gained substantial interest for the treatment of critical-size bone defect, particularly along with the maturity of the 3D printing technology that is capable of turning scaffold design ideas into real implants. As titanium alloys lack surface osteogenic activity, for improved biological performance of such scaffolds, surface modification is necessary. Various coating materials and coating methods have been explored. In this study, we developed a unique surface modification method to provide the surface of 3D printed titanium scaffolds with nano-sized structure and bioactive agent. Uniform, ordered TiO2 nanotube arrays were formed by applying two-step anodization, and then mesoporous bioactive glass (MBG) was loaded into nanotubes. The results of in vitro immersion testing showed that bioactive ions, i.e., Si and Ca ions, could be steadily and continuously released from MBG into basal medium. The assessment of the responses of hBMSCs confirmed that the surface-modified scaffolds supported the adhesion and proliferation of hBMSCs, indicating good surface cytocompatibility. The developed method of combining surface nanostructure and bioactive agent could be used as a new strategy to improve the osteogenic activity of 3D printed titanium alloy scaffolds.
...
Titanium alloy scaffolds have recently gained substantial interest for the treatment of critical-size bone defect, particularly along with the maturity of the 3D printing technology that is capable of turning scaffold design ideas into real implants. As titanium alloys lack surface osteogenic activity, for improved biological performance of such scaffolds, surface modification is necessary. Various coating materials and coating methods have been explored. In this study, we developed a unique surface modification method to provide the surface of 3D printed titanium scaffolds with nano-sized structure and bioactive agent. Uniform, ordered TiO2 nanotube arrays were formed by applying two-step anodization, and then mesoporous bioactive glass (MBG) was loaded into nanotubes. The results of in vitro immersion testing showed that bioactive ions, i.e., Si and Ca ions, could be steadily and continuously released from MBG into basal medium. The assessment of the responses of hBMSCs confirmed that the surface-modified scaffolds supported the adhesion and proliferation of hBMSCs, indicating good surface cytocompatibility. The developed method of combining surface nanostructure and bioactive agent could be used as a new strategy to improve the osteogenic activity of 3D printed titanium alloy scaffolds.