Bacterial alginate-like exopolymers (ALE) gels have been used in this work as a model for the extracellular polymeric matrix of biofilms. Aim was to relate the mechanical properties and strength of this matrix that make biofilms as persistent to cleaning as they are, to the complex cohesive molecular interactions involved. Mechanical properties of the gels as a function of CaCO₃ concentration were investigated using dynamic and static rheology. Gels with relatively low CaCO₃ concentrations, between 100 μmol and 300 μmol per g ALE, were found to exhibit similar viscoelastic behaviour as real biofilms, with elastic moduli between 50 Pa and 100 Pa and dissipation factors between 0.2 and 0.3. Increasing CaCO₃ concentrations resulted in an increase of the elastic modulus up to 250 Pa, accompanied by an increase in brittleness. At a CaCO₃ concentration of 1250 μmol per g ALE this trend stopped, probably due to disturbance of the continuous ALE network by precipitation of salts. Therefore, overdosing of Ca salts can be an adequate approach for the removal of biofouling. All gels exhibited permanent strain hardening under medium strain, and their mechanical properties showed dependency on their strain history. Even after application of an oscillatory strain with 200% amplitude that caused the gel structure to collapse, the gels recovered 65 to 90% of their original shear modulus, for the major part within the first 20 s. Recovery was slightly less for gels with high CaCO₃ concentration. In creep tests fitted with a Burgers model with multiple Kelvin elements at least three different interactions in the ALE gels could be distinguished with characteristic retardation times in the range of 10, 100 and 1000 s. Further identification of the mechanisms underlying the gel mechanics will allow the development of targeted strategies to undermine the mechanical strength of biofouling and aid the cleaning process.

Reversible attachment on soft substrates is useful in a range of applications, including soft robotics and soft-tissue surgical instrumentation. On rigid substrates, the use of micropatterned adhesives has been extensively explored. It has been shown that surface micropatterns provide conformability, thereby enabling the formation and preservation of contact with the substrate. On soft, deformable substrates, on the other hand, surface micropatterns largely lose their functionality. Alternative mechanisms have to be explored to maximize conformability and thus formation and preservation of contact on soft substrates. 3D-printing is used to fabricate adhesives with internal cylindrical pores of various configurations leading to different combinations of high/low normal/shearing stiffness, and shear forces are measured on glass and on soft elastomeric substrates. On the glass substrate, shear forces are highest for the adhesives with the lowest normal stiffness, independently from their shear stiffness. On the soft substrates, the highest shear forces are achieved for the adhesives combining low normal stiffness, enabling contact formation, with high shear stiffness, promoting contact preservation. The beneficial effect of such anisotropic stiffness on shear forces increased with the deformability of the substrate.