Since welded joints in structures are known to be critical regions for crack initiation and growth, study of fatigue crack growth behavior of welded joints under various loading scenarios are essential. In present study, two groups of experiments were conducted. At first, fatigue crack growth behavior of Al5083 butt welded joint subjected to mixed mode loading with constant amplitude has been studied. Afterwards, fatigue crack growth behavior of butt welded joints subjected to mixed mode single overload has been investigated. The sensitivity of the crack growth retardation behavior to post-welding heat treatments was also studied. Considering the effect of residual stress on fatigue crack growth, a modification to the Wheeler model was proposed to improve the accuracy of retardation prediction after applying a mixed mode overload.

Fatigue is a major cause of failure in several industries, and in many practical cases, local mixed-mode conditions prevail at the crack front. The effect of plane mode mixity on the crack growth rate and crack growth direction has been investigated. Fatigue crack growth experiments have been conducted on aluminum alloy Al5083-H111 for several mode mixities. A fixture was manufactured in order to apply the different combinations of mode I and II by changing loading angle. Afterward, three-dimensional simulations have been implemented using the Zencrack software. Based on numerical simulations, new relations are proposed to estimate stress intensity factors for compact tension shear geometry by modifying Richard’s equations [1].

The effect of mixed mode overload on the retardation of pure mode I cyclic loading has been investigated experimentally on Al5083-H111. Two models for extension of the Wheeler retardation model are proposed in order to calculate retardation of fatigue crack growth subjected to mixed mode overload. The first proposed model can predict retardation with high precision. The second proposed model is a simplified form of the first one and does not contain more experimental constants than the Wheeler model so, it may be more practical. The application of the proposed models has been examined for another material and testing conditions.

Redistribution of residual stress during crack growth in butt welded joint of Al5083-H111 was studied. Furthermore, the effect of post weld heat treatment and removing the weld reinforcements on fatigue crack growth rate was investigated. Three dimensional simulations of welding process and fatigue crack growth were conducted. It was shown that removing the weld reinforcements causes an increase in the residual stress. A correlation between the fatigue crack growth rate data of welded joints can be obtained with that of the parent metal by considering the weld geometry and redistribution of residual stresses in calculation of stress intensity factor.