Morphology of ply drops in thermoplastic composite materials manufactured using laser-assisted tape placement
D.M.J. Peeters (Mary Immaculate College, TU Delft - Aerospace Manufacturing Technologies)
Michael Deane (Mary Immaculate College)
R. O'Higgins (Mary Immaculate College)
Paul M. Weaver (Mary Immaculate College)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
Mechanical properties of composite laminates can be tuned by either tailoring ply orientations or by using ply drops to change thickness profiles. The latter cause resin-rich pockets to form in thermoset composites that are autoclave cured after lay-down. This paper focuses on the morphology of ply drop regions with carbon fibre thermoplastic composites manufactured using in-situ consolidation with laser-assisted tape placement. Our work shows that when laying a 0° ply (parallel to the ply drop) over a ply drop then the ply readily conforms to the shape of the ply drop, eliminating voids. However, when a 90° ply covers a ply drop, the processing direction affects behaviour. When the ply ascends a ply drop, a void is created. On the other hand, when the ply descends a ply drop, the substrate changes its shape due to combined laser heat and roller pressure, leading to significantly smaller voids.
help_outline