Application of physical and numerical simulations for interpretation of peripheral coarse grain structure during hot extrusion of AA7020 aluminum alloy

Application of physical and numerical simulations for interpretation of peripheral coarse grain structure during hot extrusion of AA7020 aluminum alloy

Eivani, A.R. (Iran University of Science and Technology)
Zhou, J. (TU Delft Biomaterials & Tissue Biomechanics)

2017

In this research, hot compression test is used to simulate the metallurgical phenomena occurring in the peripheral part of AA7020 aluminum alloy extrudates during hot extrusion and leading to the formation of the peripheral coarse grain (PCG) structure. The temperature profiles at a tracking point in the peripheral part of extrudates are predicted using finite element method (FEM). A special thermal treatment representing the predicted thermal profiles during extrusion is designed and applied to specimens after hot-compression testing. The effects of deformation conditions, i.e., temperature and strain rate, and the subsequent special thermal treatment on the formation of coarse grains in the AA7020 alloy are investigated. The as-deformed microstructures of specimens as well as the microstructures of specimens after the special thermal treatment are examined and the average grain size and homogeneity of grain size distribution determined. It is observed that with increasing deformation temperature or decreasing strain rate, the average recrystallized grain size increases. A fine and homogenous grain structure is obtained by increasing strain rate. According to the results of this investigation, formation of coarse grains at the periphery of the extrudate is attributed to high temperatures raised during extrusion rather than high strain rates.

Hot compression
Numerical simulation
Peripheral coarse grain
Physical simulation
Recrystallization

http://resolver.tudelft.nl/uuid:99aa9a04-95bc-4fd4-8582-1e4891b9dffa

https://doi.org/10.1016/j.jallcom.2017.06.297

2019-07-18

0925-8388

Journal of Alloys and Compounds, 725, 41-53

Accepted Author Manuscript

Institutional Repository

journal article

© 2017 A.R. Eivani, J. Zhou