Schijve, J. (author), Jacobs, F.A. (author), Tromp, P.J. (author)Comparative flight-simulation tests on four types of joints of 2024- T3 sheet material were carried out with and without application of the penetrant LPS-3. Types of joints were douhle strap joint with hi-lok bolts, asymmetric strap joint, lap joint with countersunk rivets and lap joint with dimpled holes. Observations on slip during the fatigue...report 1977
- document
- Misawa, H. (author), Schijve, J. (author) report 1986
- document
- Schijve, J. (author) report 1991
- document
- Schijve, J. (author) report 1983
- document
- Schijve, J. (author) report 1989
- document
-
Schijve, J. (author), de Rijk, P. (author)Full-scale fatigue tests were previously carried out on wing tension skins under random flight loading, program loading and constant-amplitude loading. Tension skins left from these tests were partly stripped. Tensile test revealed fatigue crack nuclei at various locations. Results have some meaning with respect to the frequency of occurrence of...report 1967
- document
- Schijve, J. (author) report 2014
- document
- Schijve, J. (author) report 1981
- document
- Schijve, J. (author) report 1993
- document
- Nederveen, A. (author), de Rijk, P. (author), Broek, D. (author), Schijve, J. (author) report 1964
- document
- Schijve, J. (author) report 1980
- document
- Schijve, J. (author) report 1981
- document
- Schijve, J. (author) report 1979
- document
- Schijve, J. (author) report 1984
- document
-
Jacobs, F.A. (author), Schijve, J. (author), Tromp, P.J. (author)Fatigue tests under flight-simulation loading have been performed on unnotched Alclad 2024-T3, anodised 2.0 mm thick sheet specimens, manufactured according to several machine-shop processes applied in the air craft industry. From the results it appears that milling is preferable to stamping. Rounding off the edges is also advantageous. The...report 1977
- document
- Schijve, J. (author) report 1979
- document
-
The fatigue life of unnotched and notched 2024-T3 Alclad sheet material from different manufacturersSchijve, J. (author)Constant-amplitude and programme-fatigue tests were carried out on unnotched specimens, central-hole specimens and riveted lap joints. Several comparisons between the results for different manufactures were made and scatter was studied. Data from the literature and correlations with other properties were analysed. Similar comparative test series...report 1968
- document
- Schijve, J. (author) report 1986
- document
- Vogelesang, L.B. (author), Marissen, R. (author), Schijve, J. (author) report 1981
- document
-
Schijve, J. (author), Jacobs, F.A. (author), Tromp, P.J. (author)A large number of flight-simulation tests were carried out on sheet specimens of 7075-T6 and 2024-T3 clad material. A gust load spectrum was adopted and a flight-by-flight loading was applied. The investigation is essentially concerned with macro-crack propagation though a few exploratory tests were conducted on the crack nucleation period. The...report 1968