Analysis of Stochastic Matrix Crack Evolution in CFRP Cross-Ply Laminates under Fatigue Loading

The present work aims at understanding the stochastic matrix crack evolution in CFRP cross-ply laminates under tension–tension fatigue loading. An experimental campaign was carried out on twenty-three specimens at different stress levels, while two optical techniques were used for the in-situ monitoring of the accumulation of transverse...

Unfolding the Early Fatigue Damage Accumulation for Cross-ply Laminates

Fatigue damage of composite laminates has attracted considerable attention from research community and industry, in view that laminated structures are inevitable to suffer from fatigue loading during their service life. It is rather complicated to understand and explain, what governs the initiation, accumulation, interaction (synergy or...