In this work, porosity-property relationships of quasi-brittle materials are explored through a combined experimental and numerical approach. In the experimental part, hemihyrate gypsum plaster powder (CaSO 4 ⋅1/2H 2 O CaSO4⋅1/2H2O) and expanded spherical polystyrene beads (1.5–2
...
The evaluation of deformation and fracture of Gilsocarbon graphite subject to service environments
Experimental and modelling
Commercial graphites are used for a wide range of applications. For example, Gilsocarbon graphite is used within the reactor core of Advanced Gas Cooled Reactors (UK) as a moderator. In service, the mechanical properties of the graphite are changed as a result of neutron irradiat
...
The evaluation of deformation and fracture of Gilsocarbon graphite subject to service environments
Experimental and modelling
Commercial graphites are used for a wide range of applications. For example, Gilsocarbon graphite is used within the reactor core of Advanced Gas Cooled Reactors (UK) as a moderator. In service, the mechanical properties of the graphite are changed as a result of neutron irradiat
...
The evaluation of deformation and fracture of Gilsocarbon graphite subject to service environments
Experimental and modelling
Commercial graphites are used for a wide range of applications. For example, Gilsocarbon graphite is used within the reactor core of Advanced Gas Cooled Reactors (UK) as a moderator. In service, the mechanical properties of the graphite are changed as a result of neutron irradiat
...
Two linked models have been developed to explore the relationship between the amount of porosity arising in service from both radiolytic oxidation and fast neutron damage that influences both the strength and the force-displacement (load-displacement) behaviour and crack propagat
...
Deformation and fracture of materials are usually considered in terms of brittle and ductile modes. However, there is an intermediate class between these limits that is termed quasi-brittle where there is measurable inelastic deformation prior to final graceful ‘brittle’ failure.
...
In quasibrittle materials the addition of specific microstructural features such as porosity can lead to departure from linear elastic behaviour prior to maximum force, followed by graceful failure. A simple but extreme example is reticulated vitreous carbon foam, with its opence
...