A microporous Al trimesate-based metal-organic framework (MOF), denoted MIL-96-(Al), was selected as a porous hybrid filler for the processing of mixed matrix membranes (MMMs) for CO₂/N₂ postcombustion separation. First, the structural model of MIL-96-(Al) initially reported was revisited using a combination of synchrotron-based single-crystal X-ray diffraction, solid-state nuclear magnetic resonance spectroscopy, and density functional theory (DFT) calculations. In a second step, pure MIL-96-(Al) crystals differing by their size and aspect ratio, including anisotropic hexagonal platelets and nanoparticles of about 70 nm in diameter, were prepared. Then, a combination of in situ IR spectroscopy, single-gas, and CO₂/N₂ coadsorption experiments, calorimetry, and molecular simulations revealed that MIL-96-(Al) nanoparticles show a relatively high CO₂ affinity over N₂ owing to strong interactions between CO₂ molecules and several adsorption sites such as Al³⁺ Lewis centers, coordinated water, and hydroxyl groups. Finally, the high compatibility between MIL-96-(Al) nanoparticles and the 6FDA-DAM polymer allowed the processing of homogeneous and defect-free MMMs with a high MOF loading (up to 25 wt %) that outperform pure polymer membranes for CO₂/N₂ separation.

Adsorption of CO₂ on MIL-53(Al) and NH₂-MIL-53(Al) has been studied by Fourier transform infrared (FTIR) spectroscopy at different temperatures and equilibrium pressures. For better interpretation of the spectra ¹³CO₂ was also utilized. It is established that with both samples at low coverages CO₂ forms O-bonded complexes with the structural OH groups (OH⋯O¹²CO). These species are characterized by μ₃(¹²CO₂) at 2337-2338 cm^-1 and two μ₂(¹²CO₂) modes around 662 and 650 cm^-1. Simultaneously, the μ(OH) modes of the hydroxyl groups are red-shifted, while the δ(OH) modes are blue-shifted. At higher coverages (OH⋯O¹²CO)₂ dimeric species are formed and this leads to a decrease of the μ₃(CO₂) frequency by 2-4 cm^-1. This change is due to vibrational interaction as proven by the observation that the frequency remains practically unaffected for (OH⋯O¹²CO) (OH⋯O¹³CO) dimeric species. Interaction between dimers leads to additional slight decrease of the value of μ₃(CO₂). In parallel with the CO₂ adsorption a partial transformation of the material from large-pore to narrow-pore form occurs. Far before CO₂ interacts with all hydroxyl groups, polymeric CO₂ species are produced within the MIL-53(Al) sample. They are characterized by a split μ₃(CO₂) mode with a pronounced component at 2340 cm^-1. The formation of these species involves some of the dimers and is accompanied by a reopening of the MIL-53 structure. Analysis of the shift of the OH modes led to the conclusion that the polymeric moiety interacts strongly with one OH group and more weakly with several other hydroxyls. No polymeric species were observed with the NH₂-MIL-53(Al) sample which is associated with the more stable narrow-pore structure of this material. However, evidence of interaction between CO₂ and the hydroxyls H-bonded to amino groups was found.