The knowledge of the structural and compositional details of Si/BaSi2/Si heterostructure annealed at high temperature is a prerequisite for BaSi2 application in heterojunction thin-film solar cells. For this purpose, Si/BaSi2/Si heterostructures deposited by magnetron sputtering with different Si layer thickness are submitted to systematic structural and compositional characterizations. Results reveal a BaSi2/Si heterointerfacial variation caused by surface oxidation and Ba diffusion at the high temperature. Its effects on the optical and electrical properties of Si/BaSi2/Si heterostructure are presented. The outcomes of this work can be extended to BaSi2 deposited by other techniques, and generate substantial advantages in BaSi2 development ranging from improvement on material qualities and eventual deployment in thin-film solar cells.@en

We compared the morphology and Raman response of nanoscale shaped surfaces of Si substrates versus monocrystalline Si. Samples were structured by reactive ion etching, and four of them were covered by a RuO2-IrO2 layer. Raman bands, centred at approx. 520 cm–1, belonging to samples processed by etching the Si surface have intensities higher by approximately one order of magnitude than those of reference non-etched samples. For nanostructured samples, the rise in the Raman signal was 12–14 ×, which is in agreement with the model of the electric field at the tips of Si due to their geometry. This phenomenon is related to the high absorption of excitation radiation. Nanostructured surfaces of samples containing a layer of RuO2-IrO2 give rise to the phenomenon of surface enhancement of the Raman response most likely due to the charge transfer at the interface between silicon and conductive oxides. The nanostructured surface of Si without a metal layer behaves as a SERS substrate and detects the analytes at a low concentration.@en

As a potential absorber candidate for high-efficient solar cell applications, BaSi2 films are confronted with issues of surface oxidation associated with the higherature annealing. Herein, BaSi2 films are deposited by the sputtering technique. A vacuum annealing process is subsequently carried out to crystallize sputtered BaSi2 films. Raman spectroscopy is used to study surface structures and crystalline quality. Elemental depth profile is measured by Auger Electron spectroscopy to understand the compositions of films. Optical and electrical properties are further investigated to reveal the effects of annealing condition. Applying vacuum annealing condition can effectively suppress diffusions of Ba and ensures a stochiometric BaSi2 layer. However, surface oxidation still occurs even in the vacuum environment owing to the high reactivity of Ba. Further attempts to prevent BaSi2 surface oxidation may focus on the combination of other methods, such as capping layer and reducing atmosphere, with vacuum (or low-pressure) annealing condition.@en