Diffusive dielectric materials such as white paint have been demonstrated as effective back reflectors in the photovoltaic technology. In this work, a one-dimensional (1D) optical modeling approach for simulation of white paint films is developed and implemented in a 1D optical simulator for thin-film solar cells. The parameters of white paint, such as the paint film thickness, the pigment volume concentration (PVC), and the pigment/binder refractive index ratio (RIR), are examined and optimized to achieve the required optical properties for back reflector application. The simulation trends indicate that white paint back reflectors with sufficient film thickness and higher PVC and RIR values exhibit improved reflectivity characteristics which results in an increased long-wavelength quantum efficiency of thin-film silicon solar cells. The simulation results based on the 1D model agree very well with the experimental data obtained from reflectance measurements of various white paint compositions and quantum efficiency measurements of amorphous silicon solar cells with white paint back reflectors.@en

In this work, we investigate the concept of transparent conductive oxide (TCO)/white paint (WP) back reflectors as an alternative to the conventional textured metal-based reflectors in thin-film silicon solar cells. The optical characterisation results show that WP back reflectors exhibit good reflectivity and excellent light scattering properties which can lead to enhanced light confinement within the thin absorber layers of the cell. To confirm this, ZnO:Al/WP reflectors with WP films of different pigment volume concentration and thickness are tested in thin-film amorphous silicon solar cells. The external quantum efficiency measurements indicate that by employing ZnO:Al/WP reflectors, good solar cell performance can be achieved, which is comparable to the performance of the cell with the conventional TCO/Ag reflector. Finally, optical simulations are employed to study the potential for further improvements in cell performance as a result of the optimisation of TCO/WP reflectors.@en

One-dimensional photonic crystals having desired broad region of high reflectance (R) were fabricated by alternating the deposition of amorphous silicon and amorphous silicon nitride layers. The effect of the deposition temperature and angle of incidence on the optical properties of photonic crystals deposited on glass substrate was determined and an excellent matching was found with the simulated results. The broad region of high R of photonic crystals deposited on flat and textured ZnO:Al substrates decreases when compared to the R of photonic crystals de-posited on glass. The performance of amorphous silicon solar cells with 1-D photonic crystals integrated as the back reflector was evaluated. The external quantum efficiency measurement demonstrated that the solar cells with the photonic crystals back reflector had an enhanced re-sponse in the long wavelength region (above 550 nm) compared to the cells with the Ag reflector.@en