The United States Air Force (USAF) Guidelines for the Durability and Damage Tolerance (DADT) certification of Additive Manufactured (AM) parts states that the most difficult challenge for the certification of an AM part is to establish an accurate prediction of its DADT. How to address this challenge is the focus of the present paper. To this end this paper examines the variability in crack growth in tests on additively manufactured (AM) Ti-6Al-4V specimens built using selective layer melting (SLM). One series of tests analysed involves thirty single edge notch tension specimens with five build orientations and two different post heat treatments. The other test program analysed involved ASTM standard single edge notch specimens with three different build directions. The results of this study highlight the ability of the Hartman–Schijve crack growth equation to capture the variability and the anisotropic behaviour of crack growth in SLM Ti-6Al-4V. It is thus shown that, despite the large variability in crack growth, the intrinsic crack growth equation remains unchanged and that the variability and the anisotropic nature of crack growth in this test program is captured by allowing for changes in both the fatigue threshold and the cyclic fracture toughness.

Understanding and characterizing crack growth is central to meeting the damage tolerance and durability requirements delineated in USAF Structures Bulletin EZ-SB-19-01 for the utilization of additive manufacturing (AM) in the sustainment of aging aircraft. In this context, the present paper discusses the effect of differentAMprocesses, different build directions, and the variability in the crack growth rates related to AM Ti-6Al-4V, AM Inconel 625, and AM 17-4 PH stainless steel. This study reveals that crack growth in these three AM materials can be captured using the Hartman-Schijve crack growth equation and that the variability in the various da/dN versus DK curves can be modeled by allowing the terms DKthr and A to vary. It is also shown that for the AM Ti-6AL-4V processes considered, the variability in the cyclic fracture toughness appears to be greatest for specimens manufactured using selective layer melting (SLM).