Xe is only produced by cryogenic distillation of air, and its availability is limited by the extremely low abundance. Therefore, Xe recovery after usage is the only way to guarantee sufficient supply and broad application. Herein we demonstrate DD3R zeolite as a benchmark membrane material for CO2/Xe separation. The CO2 permeance after an optimized membrane synthesis is one order magnitude higher than for conventional membranes and is less susceptible to water vapour. The overall membrane performance is dominated by diffusivity selectivity of CO2 over Xe in DD3R zeolite membranes, whereby rigidity of the zeolite structure plays a key role. For relevant anaesthetic composition (<5 % CO2) and condition (humid), CO2 permeance and CO2/Xe selectivity stabilized at 2.0×10−8 mol m−2 s−1 Pa−1 and 67, respectively, during long-term operation (>320 h). This endows DD3R zeolite membranes great potential for on-stream CO2 removal from the Xe-based closed-circuit anesthesia system. The large cost reduction of up to 4 orders of magnitude by membrane Xe-recycling (>99+%) allows the use of the precious Xe as anaesthetics gas a viable general option in surgery.@en

Capture and storage of the long-lived 85Kr is an efficient approach to mitigate the emission of volatile radionuclides from the spent nuclear fuel reprocessing facilities. However, it is challenging to separate krypton (Kr) from xenon (Xe) because of the chemical inertness and similar physical properties. Herein we prepared high-silica CHA zeolite membranes with ultra-high selectivity and irradiation stability for Kr/Xe separation. The suitable aperture size and rigid framework endures the membrane a strong size-exclusion effect. The ultrahigh selectivity of 51–152 together with the Kr permeance of 0.7–1.3×10−8 mol m−2 s−1 Pa−1 of high-silica CHA zeolite membranes far surpass the state-of-the-art polymeric membranes. The membrane is among the most stable polycrystalline membranes for separation of humid Kr/Xe mixtures. Together with the excellent irradiation stability, high-silica CHA zeolite membranes pave the way to separate radioactive Kr from Xe for a notable reduction of the volatile nuclear waste storage volume.@en

High-silica CHA zeolite membranes are highly desired for natural gas upgrading because of their separation performance in combination with superior mechanical and chemical stability. However, the narrow synthesis condition range significantly constrains scale-up preparation. Herein, we propose a facile interzeolite conversion approach using the FAU zeolite to prepare SSZ-13 zeolite seeds, featuring a shorter induction and a longer crystallization period of the membrane synthesis on hollow fiber substrates. The membrane thickness was constant at ~3 μm over a wide span of synthesis time (24-96 h), while the selectivity (separation efficiency) was easily improved by extending the synthesis time without compromising permeance (throughput). At 0.2 MPa feed pressure and 303 K, the membranes showed an average CO2 permeance of (5.2±0.5)×10−7 mol m−2 s−1 Pa−1 (1530 GPU), with an average CO2/CH4 mixture selectivity of 143±7. Minimal defects ensure a high selectivity of 126 with a CO2 permeation flux of 0.4 mol m−2 s−1 at 6.1 MPa feed pressure, far surpassing requirements for industrial applications. The feasibility for successful scale-up of our approach was further demonstrated by the batch synthesis of 40 cm-long hollow fiber SSZ-13 zeolite membranes exhibiting CO2/CH4 mixture selectivity up to 400 (0.2 MPa feed pressure and 303 K) without using sweep gas.@en