Anodic aluminum oxide has unique and highly attractive properties, including self-ordering of porous structure during anodization. Although anodization regimes leading to formation of highly ordered porous structures had been found experimentally, many aspects of the self-organization mechanism remain unsolved. Here, the detailed in situ small-angle X-ray diffraction study of the self-ordering in porous alumina films is reported. Structure evolution kinetics was deduced by a quantitative analysis of diffraction patterns combined with electron microscopy. The rate of pore ordering is shown to have maximal value at the initial anodization stage and rapidly decreases inversely proportional to t0.2. Self-organization is shown to occur via growth of domains possessing preferential in-plane orientation and "death" of other domains, similar to Ostwald ripening governed by difference in pore growth rates for domains of different orientations. The process is accompanied by pore death and splitting making a significant impact on anodic oxides utilization in any mass-transport issues. This finding opens a novel approach for growth of highly ordered porous anodic oxide films.@en

Inverse photonic nickel-based crystal films formed by electrocrystallization of metal inside the voids of polymer artificial opal have been studied using the microradian X-ray diffraction. Analysis of the diffraction images agrees with an face-centred cubic (FCC) structure with the lattice constant a0 650 10 nm and indicates two types of stacking sequences coexisting in the crystal (twins of ABCABC... and ACBACB... ordering motifs), the ratio between them being 4:5 The transverse structural correlation length Ltran is 2.4 0.1 μm, which corresponds to a sample thickness of 6 layers. The in-plane structural correlation length L long is 3.4 0.2 μm, and the structure mosaic is of order of 10°.@en