Photonic crystal (PhC) has been studied for their potential to improve the efficiency of Cu₂ZnSnS₄ solar cells by increasing the generated photocurrent by integrating it as a back reflector with almost zero transmission through the absorption active zone of the solar cell. It was found that the thickness of PhC layers greatly affects the width of the photonic bandgap and that increasing the thickness of VO₂ causes it to shift to a higher wavelength range. The PhC layers were added at the back side of the solar cell in two different configurations: (Monoclinic (M) VO₂/TiO₂) and (Tetragonal (T) VO₂/TiO₂) via SCAPS model. The study found that the (M VO₂/TiO₂) configuration led to an enhancement of the device's efficiency from 11.02 to 12.79%, while the (T VO₂/TiO₂) reaches 16.88%. The study concluded that the PhC layers enhance the light-matter coupling and photonic coupling and improvement in the device's performance.

Studying the mechanical properties mismatching of SnSe₂/ZrS₂ 2D materials with Voigt-Reuss-Hill (VRH) schemes promise a novel structure for sensing applications. For the first time, we studied the effect of mechanical mismatching properties of SnSe₂/ZrS₂ multilayers with VRH schemes on the acoustic wave's propagation through acoustic superlattice (AS). We proposed [(SnSe₂/ZrS₂)⁴] superlattice with VRH schemes as a new THz multichannel sensor for acetonitrile sensing. The [(SnSe₂/ZrS₂)⁴] with Voigt scheme introduced several resonant peaks for acetonitrile inside the superlattice bandgap compared to Hill and Reuss schemes. The appropriate relation between resonance frequency shift and resonance bandwidth is the key to improving the multichannel sensor's sensitivity to liquid characteristics. Further, we studied the effect of low and high temperatures on our multichannel sensor. Furthermore, the highest sensitivity and resonance frequency were recorded by our AS with the Voigt scheme towards acetonitrile having values of 0.287 (GHz/(kg/m³)) and 0.237 THz at 0 °C. The results show a novel sensitivity of acetonitrile for low-temperature environments.

Gold (Au) nanoparticles trapped within Cu₂SnS₃ (CTS) thin films were effectively deposited on a low-cost glass substrate using a simple pulsed laser deposition of 15 mJ for 5 ns at a 10 Hz repetition rate. The film's structural, morphological, topography, optical, and optoelectronic properties were investigated. Highly crystalline ternary chalcogenide CTS with tetragonal symmetry and 17 nm grain size is prepared. The 110 Ω resistivity of the thin film increases up to 125 Ω indicating a negative photoresponse under visible light excitation. The decrease in the photocurrent is also observed with Cu₂SnS₃/Au/Cu₂SnS₃ sandwich ternary chalcogenide structure at resistivities values from 31 to 35 Ω and a Joule effect influence the presence of plasmonic Au nanoparticle interlayers involved a lower phonon disorder given a higher photoresponse effect as predicted from Urbach energy.