An important aspect in cartilage ageing is accumulation of advanced glycation end products (AGEs) after exposure to sugars. Advanced glycation results in cross-links formation between the collagen fibrils in articular cartilage, hampering their flexibility and making cartilage more brittle. In the current study, we investigate whether collagen cross-linking after exposure to sugars depends on the stretching condition of the collagen fibrils. Healthy equine cartilage specimens were exposed to l-threose sugar and placed in hypo-, iso-, or hyper-osmolal conditions that expanded or shrank the tissue and changed the 3D conformation of collagen fibrils. We applied micro-indentation tests, contrast enhanced micro-computed tomography, biochemical measurement of pentosidine cross-links, and cartilage surface color analysis to assess the effects of advanced glycation cross-linking under these different conditions. Swelling of extracellular matrix due to hypo-osmolality made cartilage less susceptible to advanced glycation, namely, the increase in effective Young's modulus was approximately 80% lower in hypo-osmolality compared to hyper-osmolality and pentosidine content per collagen was 47% lower. These results indicate that healthy levels of glycosaminoglycans not only keep cartilage stiffness at appropriate levels by swelling and pre-stressed collagen fibrils, but also protect collagen fibrils from adverse effects of advanced glycation. These findings highlight the fact that collagen fibrils and therefore cartilage can be protected from further advanced glycation ("ageing") by maintaining the joint environment at sufficiently low osmolality. Understanding of mechanochemistry of collagen fibrils provided here might evoke potential ageing prohibiting strategies against cartilage deterioration.

Objective: Aging can cause an increase in the stiffness of hyaline cartilage as a consequence of increased protein crosslinks. By induction of crosslinking, a reduction in the diffusion of solutions into the hyaline cartilage has been observed. However, there is a lack of knowledge about the effects of aging on the biophysical and biochemical properties of the temporomandibular joint (TMJ) cartilage. Hence, the aim of this study was to examine the biophysical properties (thickness, stiffness, and diffusion) of the TMJ condylar cartilage of horses of different ages and their correlation with biochemical parameters. Materials and methods: We measured the compressive stiffness of the condyles, after which the diffusion of two contrast agents into cartilage was measured using Contrast Enhanced Computed Tomography technique. Furthermore, the content of water, collagen, GAG, and pentosidine was analyzed. Results: Contrary to our expectations, the stiffness of the cartilage did not change with age (modulus remained around 0.7 MPa). The diffusion of the negatively charged contrast agent (Hexabrix) also did not alter. However, the diffusion of the uncharged contrast agent (Visipaque) decreased with aging. The flux was negatively correlated with the amount of collagen and crosslink level which increased with aging. Pentosidine, collagen, and GAG were positively correlated with age whereas thickness and water content showed negative correlations. Conclusion: Our data demonstrated that aging was not necessarily reflected in the biophysical properties of TMJ condylar cartilage. The combination of the changes happening due to aging resulted in different diffusive properties, depending on the nature of the solution.