This study investigates the transparent conductive oxides (TCOs) as front contact for thin-film solar cell applications by developing a bilayer design that decouples the optical and electrical functionalities. The bilayer front contact structure combines hydrogenated indium oxide (IOH) and non-intentionally doped zinc oxide (ZnO) materials. This design achieves enhanced optoelectrical properties with a mobility of 120 cm²/Vs and a carrier density of 1.97·10¹⁹ cm^-3. Notably, the bilayer outperforms the expected average of its constituent layers in both transparency and conductivity, reflecting the benefits of optimized layer architecture. When integrated as the front electrode in a hydrogenated nanocrystalline silicon (nc-Si:H) solar cell, the IOH/ZnO bilayer yields a fill factor of 64.56 % and a power conversion efficiency of 7.85 %. When using an ITO front contact, the nc-Si:H solar cell reveals a fill factor of 56.27 % and an efficiency of 6.80 %. By successfully decoupling optical and electrical properties, the optimized IOH/ZnO bilayer offers a significant advancement over single-layer TCO configurations, presenting an innovative pathway for enhanced performance in thin-film solar cell technology.

Transparent conductive oxides (TCOs) are used as front electrode of thin film silicon (TF-Si) solar cells to increase power conversion efficiency. Metal oxides doped with different materials can be deployed as TCO. The preferred TCO is usually selected using a trade-off between transparency and conductivity. This work proposes a bi-layer front contact to address the limitation of this trade-off. IOH and i-ZnO are chosen as the best candidates for such architecture due to their good opto-electrical properties. A thin layer of IOH ensures good lateral conductivity and high transparency in the visible part of the solar spectrum. An additional i-ZnO layer provides minimized parasitic absorption losses along with low transverse resistivity. The best opto-electrical properties are achieved when deposition temperature and power density are set at 25°C and 1.5 W/cm², 200°C and 2 W/cm² for IOH and i-ZnO respectively.