Helical molecules have been proposed as candidates for producing spin-polarized currents, even at room conditions, due to their chiral asymmetry. However, describing their transport mechanism in single molecular junctions is not straightforward. In this work, we show the synthesis of two novel kinds of dithia[11]helicenes to study their electronic transport in break junctions among a series of three helical molecules: dithia[n]helicenes, with n = 7, 9, and 11 molecular units. Our experimental measurements and clustering-based analysis demonstrate low conductance values that remain similar across different applied voltages and molecules. Additionally, we assess the length dependence of the conductance for each helicene, revealing an exponential decay characteristic of off-resonant transport. This behavior is primarily attributed to the misalignment between the energy levels of the molecule-electrodes system. The length dependence trend described above is supported by ab initio calculations, further confirming an off-resonant transport mechanism.

We have performed a range of in situ heating experiments of polycrystalline Bi films of 22-25 nm-thickness in a transmission electron microscope (TEM). This shows that it is possible to locally transform a polycrystalline thin film into a [111]-oriented single-crystalline film, whereby the unique feature is that the original thickness of the film is maintained, and the substrate used in our experiments is amorphous. The single-crystalline areas have been created by heating the Bi film to temperatures close to the melting temperature with additional heating by focusing of the electron beam (e-beam), which results in local melting of the film. The film does not collapse by dewetting, and upon subsequent cooling, the film transforms into a single-crystalline [111] oriented area. The observed phenomenon is attributed to the presence of a thin Bi-oxide layer on top of Bi film. We show that removal of the Bi-oxide layer by heating the film in a H₂ gas atmosphere results in changes in the Bi film thickness and dewetting upon in situ heating in the TEM.