Steel with a nominal composition of 0.25C-1.5Si-3Mn-0.023Al (mass %) was subjected to Quenching and Partitioning (Q&P) with varying parameters (quenching temperature, partitioning temperature and partitioning time) resulting in formation of multi-phase microstructure, which was thoroughly studied using X-ray (XRD) and Electron Backscatter Diffraction (EBSD). Mechanical properties of the Q&P steel were measured by tensile tests. Plastic deformation of Q&P steel at micro-scale was investigated by in situ tensile testing and digital image correlation analysis. The effect of Q&P parameters on the microstructure (phase composition, size and volume fraction of micro constituents, texture and carbon content in retained austenite) is discussed. After analyzing the mechanical properties, plastic deformation at the micro-scale and the microstructure, it is shown that the strain partitioning between phases strongly depends on the microstructure of the Q&P steel, which, in turn, can be tuned via manipulation with Q&P parameters.@en

Cold rolled sheets of a low carbon quenching and partitioning (Q&P) steel grade were subjected to heat treatment cycles, which were designed by dilatometric experiments and optimised with respect to the quenching temperature, partitioning temperature and partitioning time. Characterisation of the retained austenite was carried out by electron backscattered diffraction, whereas the carbides were studied by scanning electron microscopy (SEM) and differential scanning calorimetry. The mechanical properties were evaluated by tensile testing and linked with retained austenite fractions and carbon contents, determined by X-ray diffraction. Conclusions are drawn concerning the influence of the kinetics of partitioning on the microstructure in terms of optimal austenite fraction in the martensitic matrix, its C content and ensuing mechanical properties.@en