We use a high-pressure semicontinuous batch electrochemical reactor with a tin-based cathode to demonstrate that it is possible to efficiently convert CO2 to formic acid (FA) in low-pH (i.e., pH < pKa) electrolyte solutions. The effects of CO2 pressure (up to 50 bar), bipolar membranes, and electrolyte (K2SO4) concentration on the current density (CD) and the Faraday efficiency (FE) of formic acid were investigated. The highest FE (?80%) of FA was achieved at a pressure of around 50 bar at a cell potential of 3.5 V and a CD of ?30 mA/cm2. To suppress the hydrogen evolution reaction (HER), the electrochemical reduction of CO2 in aqueous media is typically performed at alkaline conditions. The consequence of this is that products like formic acid, which has a pKa of 3.75, will almost completely dissociate into the formate form. The pH of the electrolyte solution has a strong influence not only on the electrochemical reduction process of CO2 but also on the downstream separation of (dilute) acid products like formic acid. The selection of separation processes depends on the dissociation state of the acids. A review of separation technologies for formic acid/formate removal from aqueous dilute streams is provided. By applying common separation heuristics, we have selected liquid-liquid extraction and electrodialysis for formic acid and formate separation, respectively. An economic evaluation of both separation processes shows that the formic acid route is more attractive than the formate one. These results urge for a better design of (1) CO2 electrocatalysts that can operate at low pH without affecting the selectivity of the desired products and (2) technologies for efficient separation of dilute products from (photo)electrochemical reactors.@en

A high pressure semicontinuous batch electrolyzer is used to convert CO2 to formic acid/formate on a tin-based cathode using bipolar membranes (BPMs) and cation exchange membranes (CEMs). The effects of CO2 pressure up to 50 bar, electrolyte concentration, flow rate, cell potential, and the two types of membranes on the current density (CD) and Faraday efficiency (FE) for formic acid/formate are investigated. Increasing the CO2 pressure yields a high FE up to 90% at a cell potential of 3.5 V and a CD of ∼30 mA/cm2. The FE decreases significantly at higher cell potentials and current densities, and lower pressures. Up to 2 wt % formate was produced at a cell potential of 4 V, a CD of ∼100 mA/cm2, and a FE of 65%. The advantages and disadvantages of using BPMs and CEMs in electrochemical cells for CO2 conversion to formic acid/formate are discussed.@en