We have found that controlled Ar ion bombardment enhances the degradation of a-Si:H based surface passivation of c-Si surfaces. The decrease in the level of surface passivation is found to be independent on the ion kinetic energy (7¿70 eV), but linearly proportional to the ion fl
...
We have found that controlled Ar ion bombardment enhances the degradation of a-Si:H based surface passivation of c-Si surfaces. The decrease in the level of surface passivation is found to be independent on the ion kinetic energy (7¿70 eV), but linearly proportional to the ion flux (6×1014¿6×1015¿ions¿cm¿2¿s¿1). This result suggests that the ion flux determines the generation rate of electron¿hole pairs in a-Si:H films, by which metastable defects are created at the H/a-Si:c-Si interface. Possible mechanisms for the ion induced generation of electron¿hole pairs are discussed.@en