Direct band gap III-V semiconductors, emitting efficiently in the amber-green region of the visible spectrum, are still missing, causing loss in efficiency in light emitting diodes operating in this region, a phenomenon known as the "green gap". Novel geometries and crystal symmetries however show strong promise in overcoming this limit. Here we develop a novel material system, consisting of wurtzite AlxIn1-xP nanowires, which is predicted to have a direct band gap in the green region. The nanowires are grown with selective area metalorganic vapor phase epitaxy and show wurtzite crystal purity from transmission electron microscopy. We show strong light emission at room temperature between the near-infrared 875 nm (1.42 eV) and the "pure green" 555 nm (2.23 eV). We investigate the band structure of wurtzite AlxIn1-xP using time-resolved and temperature-dependent photoluminescence measurements and compare the experimental results with density functional theory simulations, obtaining excellent agreement. Our work paves the way for high-efficiency green light emitting diodes based on wurtzite III-phosphide nanowires.@en

Wurtzite gallium phosphide (WZ GaP) has been predicted to exhibit a direct bandgap in the green spectral range. Optical transitions, however, are only weakly allowed by the symmetry of the bands. While efficient luminescence has been experimentally shown, the nature of the transitions is not yet clear. Here we apply tensile strain up to 6% and investigate the evolution of the photoluminescence (PL) spectrum of WZ GaP nanowires (NWs). The pressure and polarization dependence of the emission together with a theoretical analysis of strain effects is employed to establish the nature and symmetry of the transitions. We identify the emission lines to be related to localized states with significant admixture of Δ_7c symmetry and not exclusively related to the Δ_8c conduction band minimum (CBM). The results emphasize the importance of strongly bound state-related emission in the pseudodirect semiconductor WZ GaP and contribute significantly to the understanding of the optoelectronic properties of this novel material.

@en

We investigated the optical properties of wurtzite (WZ) GaP nanowires by performing photoluminescence (PL) and time-resolved PL measurements in the temperature range from 4 K to 300 K, together with atom probe tomography to identify residual impurities in the nanowires. At low temperature, the WZ GaP luminescence shows donor-acceptor pair emission at 2.115 eV and 2.088 eV, and Burstein-Moss band-filling continuum between 2.180 and 2.253 eV, resulting in a direct band gap above 2.170 eV. Sharp exciton α-β-γ lines are observed at 2.140-2.164-2.252 eV, respectively, showing clear differences in lifetime, presence of phonon replicas, and temperature-dependence. The excitonic nature of those peaks is critically discussed, leading to a direct band gap of ∼2.190 eV and to a resonant state associated with the γ-line ∼80 meV above the Γ_8C conduction band edge.

@en

Thanks to their uniqueness, nanowires allow the realization of novel semiconductor crystal structures with yet unexplored properties, which can be key to overcome current technological limits. Here we develop the growth of wurtzite GaP/InxGa1-xP core-shell nanowires with tunable indium concentration and optical emission in the visible region from 590 nm (2.1 eV) to 760 nm (1.6 eV). We demonstrate a pseudodirect (δ8c-δ9v) to direct (δ7c-δ9v) transition crossover through experimental and theoretical approach. Time resolved and temperature dependent photoluminescence measurements were used, which led to the observation of a steep change in carrier lifetime and temperature dependence by respectively one and 3 orders of magnitude in the range 0.28 ± 0.04 ≤ x ≤ 0.41 ± 0.04. Our work reveals the electronic properties of wurtzite InxGa1-xP.@en