The results of phase 1 of an interlaboratory test, coordinated by the RILEM TC 267-TRM “Tests for Reactivity of Supplementary Cementitious Materials” showed that the R3 (rapid, relevant, reliable) test method, by measurement of heat release or bound water, provided the most reliable and relevant determination of the chemical reactivity of supplementary cementitious materials (SCMs), compared to other test methods. The phase 2 work, described in this paper aimed to improve the robustness of the test procedure and to develop precision statements for the consolidated test procedure. The effect of the pre-mixing and mixing conditions, and the impact of the mix design on the test method robustness were assessed and fixed for optimal conditions to carry out the R3 heat release test. The effect of the drying step was evaluated to define the R3 bound water test procedure in more detail. Finally, the robustness of the consolidated final test methods was determined by an interlaboratory study to define the precision statements.@en

RILEM TC 267 TRM– “Tests for Reactivity of Supplementary Cementitious Materials” recommends the Rapid Reliable Relevant (R3) test as a method for determining the chemical reactivity of supplementary cementitious materials (SCMs) in Portland cement blends. In this paper, the R3 test was applied to 52 materials from a wide range of conventional and alternative SCMs with the aim to validate such test. An excellent correlation was found between the cumulative heat release and the bound water determined following the R3 test method. Comparison of the R3 test results to mortar compressive strength development showed that all conventional SCMs (e.g. blast furnace slag and fly ashes) followed the same trend, with the notable exception of very reactive calcined kaolinitic clays. It is discussed, through an in-depth statistical regression analysis of the R3 reactivity test results and the 28 days relative compressive strengths, how reactivity threshold values for classification of the chemical reactivity of SCMs could be proposed based on the R3 test results.@en

The current understanding of the carbonation of alkali-activated concretes is hampered inter alia by the wide range of binder chemistries used. To overcome some of the limitations of individual studies and to identify general correlations between their mix design parameters and carbonation resistance, the RILEM TC 281-CCC working group 6 compiled carbonation data for alkali-activated concretes and mortars from the literature. For comparison purposes, data for blended Portland cement-based concretes with a high percentage of SCMs (≥ 66% of the binder) were also included in the database. A preliminary analysis of the database indicates that w/CaO ratio and w/b ratio exert an influence on the carbonation resistance of alkali-activated concretes but, contrary to what has been reported for concretes based on (blended) Portland cements, these are not good indicators of their carbonation resistance when considered individually. A better indicator of the carbonation resistance of alkali-activated concretes under conditions approximating natural carbonation appears to be their w/(CaO + Na2O + K2O) ratio. Furthermore, the analysis points to significant shortcomings of tests at elevated CO2 concentrations for low-Ca alkali-activated concretes, indicating that even at a concentration of 1% CO2, the outcomes may lead to inaccurate predictions of the carbonation coefficient under natural exposure conditions.@en

The current understanding of the carbonation and the prediction of the carbonation rate of alkali-activated concretes is complicated inter alia by the wide range of binder chemistries used and testing conditions adopted. To overcome some of the limitations of individual studies and to identify general correlations between mix design parameters and carbonation resistance, the RILEM TC 281-CCC ‘Carbonation of Concrete with Supplementary Cementitious Materials’ Working Group 6 compiled and analysed carbonation data for alkali-activated concretes and mortars from the literature. For comparison purposes, data for blended Portland cement-based concretes with a high percentage of SCMs (≥ 66% of the binder) were also included in the database. The analysis indicates that water/CaO ratio and water/binder ratio exert an influence on the carbonation resistance of alkali-activated concretes; however, these parameters are not good indicators of the carbonation resistance when considered individually. A better indicator of the carbonation resistance of alkali-activated concretes under conditions approximating natural carbonation appears to be their water/(CaO + MgOeq + Na2Oeq + K2Oeq) ratio, where the subscript ‘eq’ indicates an equivalent amount based on molar masses. Nevertheless, this ratio can serve as approximate indicator at best, as other parameters also affect the carbonation resistance of alkali-activated concretes. In addition, the analysis of the database points to peculiarities of accelerated tests using elevated CO2 concentrations for low-Ca alkali-activated concretes, indicating that even at the relatively modest concentration of 1% CO2, accelerated testing may lead to inaccurate predictions of the carbonation resistance under natural exposure conditions.@en

Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested.@en

The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.@en

The current ability to predict the carbonation resistance of alkali-activated materials (AAMs) is incomplete, partly because of widely varying AAM chemistries and variable testing conditions. To identify general correlations between mix design parameters and the carbonation rate of AAMs, RILEM TC 281-CCC Working Group 6 compiled and analysed carbonation data for alkali-activated concretes and mortars from the literature. For comparison purposes, data for blended Portland cement-based concretes with a high percentage of SCMs (≥66% of the binder) were also included in the database. The results show that the water/CaO ratio is not a reliable indicator of the carbonation rate of AAMs. A better indicator of the carbonation rate of AAMs under conditions approximating natural carbonation is their water/(CaO + MgOeq + Na2Oeq + K2Oeq) ratio, where the index ‘eq’ indicates an equivalent amount based on molar masses. This finding can be explained by the CO2 binding capacity of alkaline-earth and alkali metal ions; the obtained correlation also indicates an influence of the space-filling capability of the binding phases of AAMs, as for conventional cements. However, this ratio can serve only as an approximate indicator of carbonation resistance, as other parameters also affect the carbonation resistance of alkali-activated concretes. In addition, the analysis of the dataset revealed peculiarities of accelerated tests using elevated CO2 concentrations for low-Ca AAMs, indicating that even at the relatively modest concentration of 1% CO2, accelerated testing may lead to inaccurate predictions of their carbonation resistance under natural exposure conditions.@en