Two-photon polymerization (2PP) is an additive manufacturing technology capable of producing polymeric 3D nano- to mesoscale structures with design flexibility and sub-micron resolution. This study investigates the influence of 2PP printing parameters on the morphology and mechanical properties of solid and porous microstructures fabricated from three commercial resins: IP-Q, IP-S, and IP-polydimethylsiloxane (IP-PDMS). To evaluate micromechanical behavior, micropillar compression tests are conducted using IP-Q, which has not been extensively characterized. Porous structures retained 80–85% of the stiffness of solids for IP-Q and IP-S, and 50% for IP-PDMS. Fourier transform infrared spectroscopy showed degrees of conversion of 38% for IP-Q and 61% for IP-S and IP-PDMS. The optimal printing parameters for IP-Q micropillars were a laser power of 50 mW, slicing distance (s) of 1.2 μm, and hatching distance (h) of 1 μm. These settings correspond to a peak laser intensity of 1.58 × 10−11 W cm−2, a focal spot diameter (dxy) of 3.17 μm, a Rayleigh length (zR) of 10.13 μm, and a voxel overlap (δ) of 0.6. These conditions yielded a Young's modulus of 3.7 GPa and yield strength of 75.21 MPa. Overall, the findings emphasize the challenges of parameter optimization when introducing porosity and comparing materials. The results provide a systematic framework for tailoring 2PP processing to guide biomedical microdevice design.