Electrode–electrolyte interphases are critical determinants of the reversibility and longevity of lithium (Li)-metal batteries (LMBs). However, upon cycling, the inherently delicate interphases, formed from electrolyte decomposition, become vulnerable to chemomechanical degradation and corrosion, resulting in rapid capacity loss and thus short battery life. Here, we present a comprehensive analysis of the complex interplay between the thermodynamic and kinetic properties of interphases on Li-metal anodes, providing insights into interphase design to address these challenges. Direct measurements of ion-transport kinetics across various electrolyte chemistries reveal that interphases with high Li-ion mobility are essential for achieving dense Li deposits. Conversely, sluggish ion transport generates high-surface-area Li deposits that induce Li random stripping and the accumulation of isolated Li deposits. Surprisingly, interphases that support long cycle life do not necessarily require the formation of dense Li deposits but must avoid possible electrochemical/chemical reactions between the Li-metal deposits and electrolytes’ components. By that, in some specific electrolyte systems, isolated Li deposits can recover and electrically rejoin the active Li anodes’ mass. These findings challenge conventional understanding and establish new principles for designing durable LMBs, demonstrating that even with commercial carbonate-based electrolytes, LiNi0.8Co0.1Mn0.1O2||Cu cells can achieve high reversibility.

The formation of stable interphases on the electrodes is crucial for rechargeable lithium (Li) batteries. However, next-generation high-energy batteries face challenges in controlling interphase formation due to the high reactivity and structural changes of electrodes, leading to reduced stability and slow ion transport, which accelerate battery degradation. Here, we report an approach to address these issues by introducing multicomponent grain-boundary-rich interphase that boosts the rapid transport of ions and enhances passivation toward prolonged lifespan. This is guided by fundamental principles of solid-state ionics and geological crystallization differentiation theory, achieved through improved solvation chemistry. Demonstrations showcase how the introduction of the interphase substantially impacts the Li-ion transport across the interphase and the electrode-electrolyte compatibility in cost-effective electrolyte solutions optimized with multiple Li salts. The resulting interphases feature microstructures rich in inorganic grain boundaries with a diverse array of nanosized grains, presenting enhanced Li-ion transport. Comprehensive analyses revealed that this realizes remarkable electrochemical stability over extended cycling periods by inhibiting electrode corrosion, thus holding promise for high-capacity thin-Li-metal, Si-based anodes, and even Li-free anodes when paired with high-capacity oxide cathodes. This work opens new avenues to customize protective interphases on high-capacity electrodes, promoting the development of batteries with the highest energy density using cost-effective electrolytes.