Coupling of carbonation and chlorides ingress mechanisms is very common in concrete under certain exposure conditions such as coastal environments. The aggravation/ mitigation of corrosion by the existence of carbonation lies on the fact that microstructural changes due to carbonation result in changes on the transport properties of the material. In this study we investigate and quantify evolving transport properties of ordinary Portland cement paste, such as porosity, tortuosity and intrinsic permeability. Dual X-ray micro computed tomography (micro CT) is used for the quantification of porosity. Furthermore Dynamic Vapour Sorption (DVS) measurements are carried out to resolve water retention and relative permeability curves. The authors expect to provide insights into the mechanisms of accelerated carbonation in both types of cement paste, as well as data for input and validation of numerical and analytical models on this degradation phenomenon.

The increasing concern for safety and sustainability of structures is calling for the development of smart self-healing materials and preventive repair methods. The appearance of small cracks (<300 µm in width) in concrete is almost unavoidable, not necessarily causing a risk of collapse for the structure, but surely impairing its functionality, accelerating its degradation, and diminishing its service life and sustainability. This review provides the state-of-the-art of recent developments of self-healing concrete, covering autogenous or intrinsic healing of traditional concrete followed by stimulated autogenous healing via use of mineral additives, crystalline admixtures or (superabsorbent) polymers, and subsequently autonomous self-healing mechanisms, i.e. via, application of micro-, macro-, or vascular encapsulated polymers, minerals, or bacteria. The (stimulated) autogenous mechanisms are generally limited to healing crack widths of about 100–150 µm. In contrast, most autonomous self-healing mechanisms can heal cracks of 300 µm, even sometimes up to more than 1 mm, and usually act faster. After explaining the basic concept for each self-healing technique, the most recent advances are collected, explaining the progress and current limitations, to provide insights toward the future developments. This review addresses the research needs required to remove hindrances that limit market penetration of self-healing concrete technologies.