Chloride-based solid electrolytes are considered interesting candidates for catholytes in all-solid-state batteries due to their high electrochemical stability, which allows the use of high-voltage cathodes without protective coatings. Aliovalent Zr(iv) substitution is a widely applicable strategy to increase the ionic conductivity of Li₃M(iii)Cl₆ solid electrolytes. In this study, we investigate how Zr(iv) substitution affects the structure and ion conduction in Li_3−xIn_1−xZr_xCl₆ (0 ≤ x ≤ 0.5). Rietveld refinement using both X-ray and neutron diffraction is used to make a structural model based on two sets of scattering contrasts. AC-impedance measurements and solid-state NMR relaxometry measurements at multiple Larmor frequencies are used to study the Li-ion dynamics. In this manner the diffusion mechanism and its correlation with the structure are explored and compared to previous studies, advancing the understanding of these complex and difficult to characterize materials. It is found that the diffusion in Li₃InCl₆ is most likely anisotropic considering the crystal structure and two distinct jump processes found by solid-state NMR. Zr-substitution improves ionic conductivity by tuning the charge carrier concentration, accompanied by small changes in the crystal structure which affect ion transport on short timescales, likely reducing the anisotropy.

The quarternary (Mn,Fe)₂(P,Si)-based materials with a giant magnetocaloric effect (GMCE) at the ferromagnetic transition T_C are promising bulk materials for solid-state magnetic refrigeration. In the present study we demonstrate that doping with the light elements fluorine and sulfur can be used to adjust T_C near room temperature and tune the magnetocaloric properties. For F doping the first-order magnetic transition (FOMT) of Mn_0.60Fe_1.30P_0.64Si_0.36F_x (x = 0.00, 0.01, 0.02, 0.03) is enhanced, which is explained by an enhanced magnetoelastic coupling. The magnetic entropy change |ΔS_m| at a field change (Δμ₀H) of 2 T markedly improved by 30% from 14.2 Jkg⁻¹K⁻¹ (x = 0.00) at 335 K to 20.2 Jkg⁻¹K⁻¹ (x = 0.03) at 297 K. For the F doped material the value of |ΔS_m| for Δμ₀H = 1 T reaches 11.6 Jkg⁻¹K⁻¹ at 294 K, which is consistent with the calorimetric data (12.4 Jkg⁻¹K⁻¹). Neutron diffraction experiments reveal enhanced magnetic moments by F doping in agreement with the prediction of DFT calculation. For S doping in Mn_0.60Fe_1.25P_0.66-ySi_0.34S_y (y = 0.00, 0.01, 0.02, 0.03, 0.04) three impurity phases have been found from microstructural analysis, which reduce the stability of the FOMT in the main phase and decrease T_C, e.g. the |ΔS_m| reduces from 7.9(12.6) Jkg^-1K^-1 (332 K) for the undoped sample to 3.4(6.2) Jkg^-1K^-1 (313 K) for the maximum doped sample for Δμ₀H = 1(2) T. Neutron diffraction experiments combined with first-principles theoretical calculation, distinguish the occupation of F/S dopants and the tuning mechanism for light element doping, corresponding to subtle structural changes and a strengthening of the covalent bonding between metal and metalloid atoms. It is found that the light elements F and S can effectively regulate the magnetocaloric properties and provide fundamental understanding of (Mn,Fe)₂(P,Si)-based intermetallic compounds.