New production routes for ⁹⁹Mo are steadily gaining importance. However, the obtained specific activity is much lower than currently produced by the fission of U-235. To be able to supply hospitals with ⁹⁹Mo/^99mTc generators with the desired activity, the adsorption capacity of the column material should be increased. In this paper we have investigated whether the gas phase coating technique Atomic Layer Deposition (ALD), which can deposit ultra-thin layers on high surface area materials, can be used to attain materials with high adsorption capacity for ⁹⁹Mo. For this purpose, ALD was applied on a silica-core sorbent material to coat it with a thin layer of alumina. This sorbent material shows to have a maximum adsorption capacity of 120 mg/g and has a^99mTc elution efficiency of 55 ± 2% based on 3 executive elutions.

To improve the stability and carrier mobility of quantum dot (QD) optoelectronic devices, encapsulation or pore infilling processes are advantageous. Atomic layer deposition (ALD) is an ideal technique to infill and overcoat QD films, as it provides excellent control over film growth at the sub-nanometer scale and results in conformal coatings with mild processing conditions. Different thicknesses of crystalline ZnO films deposited on InP QD films are studied with spectrophotometry and time-resolved microwave conductivity measurements. High carrier mobilities of 4 cm² (V s)⁻¹ and charge separation between the QDs and ZnO are observed. Furthermore, the results confirm that the stability of QD thin films is strongly improved when the inorganic ALD coating is applied. Finally, proof-of-concept photovoltaic devices of InP QD films are demonstrated with an ALD-grown ZnO electron extraction layer.