The results of phase 1 of an interlaboratory test, coordinated by the RILEM TC 267-TRM “Tests for Reactivity of Supplementary Cementitious Materials” showed that the R3 (rapid, relevant, reliable) test method, by measurement of heat release or bound water, provided the most reliable and relevant determination of the chemical reactivity of supplementary cementitious materials (SCMs), compared to other test methods. The phase 2 work, described in this paper aimed to improve the robustness of the test procedure and to develop precision statements for the consolidated test procedure. The effect of the pre-mixing and mixing conditions, and the impact of the mix design on the test method robustness were assessed and fixed for optimal conditions to carry out the R3 heat release test. The effect of the drying step was evaluated to define the R3 bound water test procedure in more detail. Finally, the robustness of the consolidated final test methods was determined by an interlaboratory study to define the precision statements.@en

RILEM TC 267 TRM– “Tests for Reactivity of Supplementary Cementitious Materials” recommends the Rapid Reliable Relevant (R3) test as a method for determining the chemical reactivity of supplementary cementitious materials (SCMs) in Portland cement blends. In this paper, the R3 test was applied to 52 materials from a wide range of conventional and alternative SCMs with the aim to validate such test. An excellent correlation was found between the cumulative heat release and the bound water determined following the R3 test method. Comparison of the R3 test results to mortar compressive strength development showed that all conventional SCMs (e.g. blast furnace slag and fly ashes) followed the same trend, with the notable exception of very reactive calcined kaolinitic clays. It is discussed, through an in-depth statistical regression analysis of the R3 reactivity test results and the 28 days relative compressive strengths, how reactivity threshold values for classification of the chemical reactivity of SCMs could be proposed based on the R3 test results.@en

This paper provides a critical review on autogenous shrinkage of alkali-activated slag (AAS). It is reported that AAS paste, mortar, and concrete generally show larger autogenous shrinkage than Portland cement (PC) counterparts. Self-desiccation is the main driving force of the autogenous shrinkage of hardened AAS, but other mechanisms also play roles, particularly at early age. Existing models developed for PC do not give satisfactory estimations of the autogenous shrinkage of AAS, unless the pronounced viscoelasticity of AAS is considered. The susceptibility of AAS concrete to extensive cracking is not necessarily high due to the effects of stress relaxation, but local creep can exacerbate the development of microcracks. Various strategies have been proposed to mitigate the autogenous shrinkage of AAS, but many exhibit side effects, e.g., strength reduction. Existing testing methods for autogenous shrinkage of PC seem applicable to AAS, but the starting time and test duration need to be reconsidered.@en

The current understanding of the carbonation of alkali-activated concretes is hampered inter alia by the wide range of binder chemistries used. To overcome some of the limitations of individual studies and to identify general correlations between their mix design parameters and carbonation resistance, the RILEM TC 281-CCC working group 6 compiled carbonation data for alkali-activated concretes and mortars from the literature. For comparison purposes, data for blended Portland cement-based concretes with a high percentage of SCMs (≥ 66% of the binder) were also included in the database. A preliminary analysis of the database indicates that w/CaO ratio and w/b ratio exert an influence on the carbonation resistance of alkali-activated concretes but, contrary to what has been reported for concretes based on (blended) Portland cements, these are not good indicators of their carbonation resistance when considered individually. A better indicator of the carbonation resistance of alkali-activated concretes under conditions approximating natural carbonation appears to be their w/(CaO + Na2O + K2O) ratio. Furthermore, the analysis points to significant shortcomings of tests at elevated CO2 concentrations for low-Ca alkali-activated concretes, indicating that even at a concentration of 1% CO2, the outcomes may lead to inaccurate predictions of the carbonation coefficient under natural exposure conditions.@en