Solid-state batteries currently receive extensive attention due to their potential to outperform lithium-ion batteries in terms of energy density when featuring next-generation anodes such as lithium metal or silicon. However, most highly conducting solid electrolytes decompose at the low operating voltages of next-generation anodes leading to irreversible lithium loss and increased cell resistance. Such performance losses may be prevented by designing electrolytes which are thermodynamically stable at low operating voltages (anolytes). Here, we report on the discovery of a new family of irreducible (i.e., fully reduced) electrolytes by mechanochemically dissolving lithium nitride into the Li₂S antifluorite structure, yielding highly conducting crystalline Li_2+xS_1-xN_x phases reaching >0.2 mS cm^-1 at ambient temperature. Combining impedance spectroscopy experiments and ab initio density functional theory calculations we clarify the mechanism by which the disordering of the sulfide and nitride ions in the anion sublattice boosts ionic conductivity in Li_2+xS_1-xN_x phases by a factor 10⁵ compared to the Li₂S host structure. This advance is achieved through a novel theoretical framework, leveraging percolation analysis with local-environment-specific activation energies and is widely applicable to disordered ion conductors. The same methodology allows us to rationalize how increasing nitrogen content in Li_2+xS_1-xN_x antifluorite-like samples leads to both increased ionic conductivity and lower conductivity-activation energy. These findings pave the way to understanding disordered solid electrolytes and eliminating decomposition-induced performance losses on the anode side in solid-state batteries.

Irreducible solid electrolytes (SEs), characterized by non-Li framework ions in their lowest oxidation states, offer intrinsic compatibility with low-reduction-potential, high-capacity negative electrodes, such as lithium metal and silicon. In these SE materials, disorder engineering and vacancy formation reduce lithium-ion diffusion barriers, achieving room-temperature ionic conductivities exceeding 0.1 mS cm^–1. Experiments and atomistic simulations confirm that irreducible SEs form decomposition-free interfaces with Li metal. Their limited oxidative stability can be addressed by pairing them with an electrolyte layer stable with practical cathodes yet demanding interface compatibility between the two electrolyte layers. Here we highlight key research directions to accelerate irreducible SE transition from laboratory to practical application, including expanding compositional diversity, optimizing interfaces with cathode-facing electrolytes, developing scalable thin-film processing, and exploring compatibility with other low working potential anodes like silicon. Addressing these challenges is essential to unlock the full potential of irreducible SEs for high-energy, long-life, all-solid-state batteries.

Solid-state batteries currently receive ample attention due to their potential to outperform lithium-ion batteries in terms of energy density when featuring next-generation anodes such as lithium metal or silicon. One key remaining challenge is identifying solid electrolytes that combine high ionic conductivity with stability in contact with the highly reducing potentials of next-generation anodes. Fully reduced electrolytes, based on irreducible anions, offer a promising solution by avoiding electrolyte decomposition altogether. In this study, we demonstrate the compositional flexibility of the disordered antifluorite framework accessible by mechanochemical synthesis and leverage it to discover irreducible electrolytes with high ionic conductivities. We show that the recently investigated Li ₉N ₂Cl ₃ and Li ₅NCl ₂ phases are part of the same solid solution of Li-deficient antifluorite phases existing on the LiCl-Li ₃N tie line with a general chemical formula of Li _1+2xCl _1−xN _x (0.33 < x < 0.5). Using density functional theory calculations, we identify the origin of the 5-order-of-magnitude conductivity increase of the Li _1+2xCl _1−xN _x phases compared to the structurally related rock-salt LiCl phase. Finally, we demonstrate that S _Cl- and Br _Cl-substituted analogues of the Li _1+2xCl _1−xN _x phases may be synthesized, enabling significant conductivity improvements by a factor of 10, reaching 0.2 mS cm ⁻¹ for Li _2.31S _0.41Br _0.14N _0.45. This investigation demonstrates for the first time that irreducible antifluorite-like phases are compositionally highly modifiable; this finding lays the ground for discovery of new compositions of irreducible antifluorite-like phases with even further increased conductivities, which could help eliminate solid-electrolyte decomposition and decomposition-induced Li losses on the anode side in high-performance next-generation batteries.