To show compliance to structural engineering codes and implement quality control measures, it is critical to obtain reliable mechanical properties of the materials in question. For conventional cast and precast concrete, the experimental procedures and relationships between mechanical properties, the material composition, and the production methods are globally known, but for 3D concrete printing (3DCP), these relations have not yet been established. Previous studies have shown little consistency in results, and the underlying experimental methods have not been established broadly. There is an urgent need to address these issues as the application of 3DCP in practice projects is growing rapidly. Therefore, RILEM TC 304-ADC: Assessment of Additively Manufactured Concrete Materials and Structures has set up a large interlaboratory study into the mechanical properties of 3D printed concrete. This paper presents key elements of the experimental approach detailed in the Study Plan and the supporting considerations. Furthermore, it reports on the response, consisting of 34 contributions from 30 laboratories, detailing global coverage, properties of the applied mixture designs and characteristics of the printing facilities that have been used. Subsequently, some fundamental results from compression, flexural, and E-modulus testing are presented and—considering cast specimens as a reference—discussed. On average, a reduction in strength was found in compression and E-modulus (all tested orientations). For flexure, on the other hand, an increase was found in two testing orientations, while a decrease was observed in the third orientation. Importantly, even though the applied experimental methods were found to be reasonably appropriate to obtain the required data, the differences found between individual contributions are significant and sometimes non-consistent, suggesting that testing on specific material-facility combinations is necessary to reliably determine the mechanical properties of objects produced from them. Furthermore, a theoretical framework needs to be developed to further explain the variations that were observed. Extensive analyses of all acquired data are out of the scope of this contribution, but presented in two associated papers, whereas a third presents the data management approach used to process the approximately 5,000 test results.

Over the last century, over one hundred crack width formulas have been developed to calculate the width and spacing of cracks in reinforced and prestressed concrete elements. It is unclear which formulas are the most accurate. An extensive comparison study is required to determine which formulas accurately describe the crack patterns, consisting of the crack width and spacing. To make such a study possible, this paper proposes categorizing formulas. The categorization of the formulas is based on their applicability, crack pattern representation, and background. The categorization presents an overview of the different assumptions and application areas for describing crack patterns.

Digital fabrication with cementitious materials is a rapidly growing field of research in which the evolution of strength during the various processes, such as 3D printing, is the key controlling parameter. The strength evolves over multiple orders of magnitude during the process, and thus, it is essential to properly characterize the strength evolution in order to guarantee process success. This chapter summarizes the state of the art in these characterization methods for digital fabrication with fresh cementitious materials, reviewing well-known and more recently developed methods.