Carbon-supported nickel and nitrogen co-doped (Ni-N-C) catalysts have been extensively studied as selective and active catalysts for CO2 electroreduction to CO. Most studies have focused on adjusting the coordination structure of Ni-Nx active sites, while the impact of the carbon supports has often been overlooked. In this study, a series of Ni-N-C catalysts on different carbon supports, including carbon black (CB), multi-walled carbon nanotubes (CNT), and activated nitrogen-doped biochar (ANBC), were synthesized using a ligand-mediated method. The effect of the carbon support on the electrocatalytic performance for CO2 reduction was investigated at both low current densities, in a H-cell, and high current densities, in a MEA electrolyzer. All of the prepared Ni-N-C catalysts show good faradaic efficiencies (FE) toward CO production (up to ∼90 %), however, the onset potentials and partial current densities for CO production vary greatly. The textural properties of the carbon support and the distribution of Ni-Nx active sites on the carbon support are demonstrated as the main factors behind the performance differences. In particular, hierarchical porous structures with a large specific surface area are helpful to facilitate mass transport and improve the dispersion of active sites, which allows for a better CO2 reduction performance of Ni-N-ANBC compared to Ni-N-CB and Ni-N-CNT. This study demonstrates the importance of the carbon support for Ni-N-C catalysts and provides new insights into the design of efficient Ni-N-C catalysts for the CO2RR.

We investigated the evaporative crystallization of aqueous glycine sessile droplets on hydrophilic glass, hydrophobic Teflon surfaces, and hydrophobic Teflon surfaces, where the contact angle is manipulated dynamically with electrowetting. Microscopy experiments and analytical characterization revealed that the size, morphology, and polymorphic form (α, β, and γ) of the glycine crystals are influenced by the surface wettability as well as the amplitude and frequency of electrowetting. On a hydrophilic glass surface, a coffee-stain-shaped residue composed of a mixture of bipyramidal α and needle-like β crystals was observed. On a hydrophobic Teflon surface, the droplets evaporated with minimum contact line pinning, producing hemispherical residue shapes, and bipyramidal α crystals smaller than 100 μm were formed. On a Teflon surface with electrowetting, glycine could be manipulated to crystallize into distinct polymorphic forms (β and γ) and residue shapes not observed on hydrophilic glass and hydrophobic Teflon surfaces. The frequency and amplitude of electrowetting were optimized to produce single large crystals. We observed the highest chance of producing single-millimeter-scale crystals at a frequency of 1 kHz and a voltage amplitude of 80 Vrms. We attribute this observation to a combination of nucleation at lower bulk supersaturation compared to the experiment on Teflon surfaces and electrowetting-induced mixing most prominent at 1 kHz. Our results highlight the opportunities arising from the dynamic manipulation of surface wettability

Worldwide, a considerable amount of oily wastewater is generated, with oil droplets from 2 to 200 nm that are difficult to separate because of their size and colloidal stability. This study presents a novel approach for effectively separating microemulsions via cubic silicon carbide (3C-SiC)-coated alumina (Al ₂O ₃) membranes fabricated based on low pressure chemical vapor deposition (LPCVD). SiC was deposited at a relatively low temperature at 860 °C on 100 nm Al ₂O ₃ membranes using two precursors: SiH ₂Cl ₂ and C ₂H ₂. With the increase in deposition time, up to 25 min, the pore size decreased from 41 nm to 33 nm, which is a smaller pore size of a SiC membrane than previously used for oil/water separation. The polycrystalline 3C-SiC-coated membranes showed improved hydrophilicity (water contact angle of 15°) and highly negatively charged surfaces (−65 mV). Microemulsion filtration experiments were carried out at a constant permeate flux (80 Lm ⁻² h ⁻¹) for six cycles with varying deposition time, pH, surfactant types, and pore sizes. The fouling of the SiC-coated membrane was, compared to the Al ₂O ₃ membrane, effectively mitigated due to the enhanced electrostatic repulsion and hydrophilicity. Surfactant adsorption mainly occurred when the surface charge of the microemulsion and the membranes were opposite. Therefore, the surface charge of the alumina membrane changed from positive to negative when soaked in negatively charged microemulsions, whereas SiC-coated membranes remained negatively charged regardless of surfactant type. The membrane fouling was alleviated when the membrane and oil droplets had the same charge. Lastly, the 62 nm SiC-coated membrane with 20 min coating time was the best choice for the filtration of the microemulsion, because of the high rejection of the oil droplets and low fouling tendency.

The increasing prevalence of calcium pyrophosphate dihydrate (CPPD) deposition disease, a form of arthritis with high inflammatory potential, has triggered considerable interest in the search for additives to prevent CPPD crystal formation, particularly in the field of biomineralization. In this context, CPPD crystallization in aqueous solution with and without glycine, glutamic acid, or glycyl-L-glutamic acid as crystal-growth modifier was experimentally investigated. The produced crystals were characterized structurally, morphologically, and in terms of their surface charge. In addition, the thermal degradation profiles of CPPD crystals obtained with and without the modifiers were characterized by TGA-FTIR, and the major volatile product was H₂O.