An ODS steel with nominal composition Fe–14Cr–2W–0.4Ti-0.3Y2O3 (wt.%) was produced by mechanical alloying and compacted by hot isostatic pressing (HIP) followed by hot cross rolling (HCR). To check the effects of thermal aging at relevant temperatures of operation in fusion power plants, the alloy was thermally aged at 873 K for 2000 h. In this work, small-angle neutron scattering (SANS) and X-ray absorption spectroscopy (XAS) techniques are used for the advanced characterization of secondary phases and the oxide nanoparticle dispersion. SANS results show that the oxide nanoparticles remain stable after the thermal aging treatment. Composition of the oxide nanoparticles was identified as Y2TiO5 or Y2Ti2O7 by SANS, while non-stoichiometry was found by XAS analysis. Laves phase precipitation after the thermal aging treatment is further confirmed by SANS, from the magnetic anisotropic contribution to the scattering intensity associated to this metallic phase, and by XANES.@en

The layered metamagnet CrSBr offers a rich interplay between magnetic, optical, and electrical properties that can be extended down to the two-dimensional (2D) limit. Despite the extensive research regarding the long-range magnetic order in magnetic van der Waals materials, short-range correlations have been loosely investigated. By using small-angle neutron scattering (SANS) the formation of short-range magnetic regions in CrSBr with correlation lengths that increase upon cooling up to ≈3 nm at the antiferromagnetic ordering temperature (T N ≈ 140 K) is shown. Interestingly, these ferromagnetic correlations start developing below 200 K, i.e., well above T N. Below T N, these correlations rapidly decrease and are negligible at low-temperatures. The experimental results are well-reproduced by an effective spin Hamiltonian, which pinpoints that the short-range correlations in CrSBr are intrinsic to the monolayer limit, and discard the appearance of any frustrated phase in CrSBr at low-temperatures within the experimental window between 2 and 200 nm. Overall, the obtained results are compatible with a spin freezing scenario of the magnetic fluctuations in CrSBr and highlight SANS as a powerful technique for characterizing the rich physical phenomenology beyond the long-range order paradigm offered by van der Waals magnets.@en

The JCNS has been developing and using in-situ polarized neutron spin filters for many applications. The system used for analysis on MARIA and polarization for TOPAS were completed about 10 years ago with the MARIA system in standard operation for users and the TOPAS system employed for a long measurement on the POLI instrument. In the meantime we are progressing on several new in-situ polarizers based on these first two but with additional innovations. The KWS-1 analyzer device which was recently used in tests at TU Delft and ISIS is essentially a 50%-sized copy of the MARIA device. The two devices in construction for polarization and analysis on POLI for hot neutrons feature magic-boxes with angled plates on both the entrance and exit sides to minimize overal length and the polarizer device will employ an additional passive magnetic shield of soft iron so that it can operate inside the stray field area of a 8-T vertical (compensated) sample magnet. We will summarize the current status of our 3He neutron spin filters and provide extra focus on the technical aspects and measured performance characteristics of the new devices for KWS-1 and POLI in particular. @en